Chevron Phillips MD6800 HIPS - High Impact Polystyrene  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips MD6800 HIPS - High Impact Polystyrene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rubber modified high impact polystyrene.Applications:Displays and retail product shelvingDurable household applicationsThin to medium thickness parts that require a combination of high flow and good toughnessFeatures:Excellent practical toughnessMedium/low glossBalance of stiffness and toughnessUL classification 94HBInformation provided by Chevron PhillipsThe Chevron Phillips polystyrene product line was transferred to Americas Styrenics in 2008.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc
1.03 g/cc
ASTM D-792
Bulk Density 0.609 - 0.673 g/cc
0.0220 - 0.0243 lb/in³
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
24 hours; ASTM D-955
Melt Flow 8.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D-1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 23.0 MPa
3340 psi
2.0 in/min; 0.125" thickness; ASTM D-638
Elongation at Yield 45 %
45 %
2.0 in/min; 0.125" thickness; ASTM D-638
Tensile Modulus 2.07 GPa
300 ksi
2.0 in/min; 0.125" thickness; ASTM D-638
Flexural Strength 41.0 MPa
5950 psi
0.1 in/min; 0.250" thickness; ASTM D-790B
Flexural Modulus 1.95 GPa
283 ksi
0.1 in/min; 0.250" thickness; ASTM D-790B
Izod Impact, Notched 1.17 J/cm

@Thickness 3.17 mm,
Temperature 22.8 °C
2.19 ft-lb/in

@Thickness 0.125 in,
Temperature 73.0 °F
ASTM D-256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C

@Thickness 6.35 mm
172 °F

@Thickness 0.250 in
ASTM D-648
Vicat Softening Point 94.0 °C

@Thickness 6.35 mm
201 °F

@Thickness 0.250 in
Rate B; ASTM D-1525
Flammability, UL94 HB
HB