Material Notes:
High heat crystal polystyrene.Applications:Medical partsConsumer containers, vials, jars, etc.Clock lensesAudio cassettesFeatures:Fast cycling due to high heat distortionHigh Vicat softening temperatureExcellent clarityBalanced flow - heat distortion characteristicsInformation provided by Chevron PhillipsThe Chevron Phillips polystyrene product line was transferred to Americas Styrenics in 2008.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc
1.03 g/cc
ASTM D-792
Bulk Density 0.609 - 0.673 g/cc
0.0220 - 0.0243 lb/in³
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
24 hours; ASTM D-955
Melt Flow 7.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
7.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D-1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 51.0 MPa
7400 psi
0.2 in/min; 0.125" thickness; ASTM D-638
Elongation at Yield 4.5 %
4.5 %
0.2 in/min; 0.125" thickness; ASTM D-638
Tensile Modulus 3.10 GPa
450 ksi
0.2 in/min; 0.125" thickness; ASTM D-638
Flexural Strength 69.0 MPa
10000 psi
0.1 in/min; 0.250" thickness; ASTM D-790B
Flexural Modulus 3.10 GPa
450 ksi
0.1 in/min; 0.250" thickness; ASTM D-790B
Izod Impact, Notched 0.190 J/cm

@Thickness 3.17 mm,
Temperature 22.8 °C
0.356 ft-lb/in

@Thickness 0.125 in,
Temperature 73.0 °F
ASTM D-256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C

@Thickness 6.35 mm
194 °F

@Thickness 0.250 in
ASTM D-648
Vicat Softening Point 107 °C

@Thickness 6.35 mm
225 °F

@Thickness 0.250 in
Rate B; ASTM D-1525