Chevron Phillips K-Resin® KR05NW Styrene-Butadiene Copolymer, Sheet and Blow Mold Grade

Category Polymer , Thermoplastic , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC
Manufacturer Chevron Phillips Chemical Company LP
Trade Name K-Resin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips K-Resin® KR05NW Styrene-Butadiene Copolymer, Sheet and Blow Mold Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Styrene-Butadiene Copolymer. No wax (NW) form of K-Resin® KR05 to facilitate printing.Customer Benefits: This SBC is easily processed on blow molding or extrusion and thermoforming equipment. Finished products have excellent clarity, good toughness, good stiffness, high surface gloss, good formability. KR05NW is the no wax form of KR05 to facilitate printing and decorating.Applications: Major applications include bottles, profiles, displays, containers, and unblended sheet.Processing Recommendations:Sheet Extrusion: Melt Temperature, 218°C maximum. High shear and restrictive type screws tend to degrade the melt. Generally no need to dry resin. Blow Molding: 188-196°C for maximum melt strength. Generally no need to dry resin. Injection Blow Molding: Melt Temperature, 232°C maximum. Generally no need to dry resin.Specification Data: FDA Regulation 21 CFR 177.1640. Suitable for food contact. EEC Directive 90/128/EEC and all its amendments. USP Class VI-50. UL 94HB.Data provided by Chevron Phillips Chemical Company LP.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ASTM D792
Water Absorption 0.090 %
0.090 %
ASTM D570
Melt Flow 7.5 g/10 min

@Load 5.00 kg,
Temperature 200 °C
7.5 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 65
65
ASTM D2240
Tensile Strength, Yield 26.0 MPa
3770 psi
Type 1 @ 2 in/min; ASTM D638
Elongation at Break 160 %
160 %
Type 1 @ 2 in/min; ASTM D638
Flexural Yield Strength 34.0 MPa
4930 psi
ASTM D790
Flexural Modulus 1.413 GPa
204.9 ksi
ASTM D790
Izod Impact, Notched 0.410 J/cm

@Thickness 3.17 mm
0.768 ft-lb/in

@Thickness 0.125 in
ASTM D256
Impact Test 29.7 J

@Thickness 3.17 mm
21.9 ft-lb

@Thickness 0.125 in
Instrumented Total Energy; @ 150 in/sec impact rate; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
ASTM D648
Vicat Softening Point 87.0 °C
189 °F
Condition B (50N); ASTM D1525
Flammability, UL94 HB
HB
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
ASTM D1003
Processing Properties Metric English Comments
Processing Temperature <= 218 °C
<= 424 °F
sheet extrusion