Chevron Phillips HiD® 9647T HDPE Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips HiD® 9647T HDPE Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: Linear Polyethylene CopolymerCharacteristics: Copolymerization Enhances Film Toughness, Unique Combination of Density and Melt Index, Excellent Strength Properties as well as Good Heat Seal, Lower Density Imparts a Softer Feel and Lesser Tendency to Wrinkle, Even with Lower Density - Produces a Film with Significant StiffnessApplications:Draw Tapes, High Tensile Films. Recommended Die Gap: 0.89 mm.Film properties below based on film thickness of 25.4 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.939 g/cc
0.0339 lb/in³
ASTM D1505
Moisture Vapor Transmission 0.200 cc-mm/m²-24hr-atm
0.508 cc-mil/100 in²-24hr-atm
ASTM F1249
Melt Flow 0.20 g/10 min
0.20 g/10 min
Condition E; ASTM D 1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 420 %
420 %
ASTM D882
Film Elongation at Break, TD 630 %
630 %
ASTM D882
Secant Modulus, MD 0.520 GPa
75.4 ksi
ASTM D882
Secant Modulus, TD 0.660 GPa
95.7 ksi
ASTM D882
Elmendorf Tear Strength, MD 0.630 g/micron
16.0 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 26.4 g/micron
670 g/mil
ASTM D1922
Dart Drop 2.70 g/micron
68.6 g/mil
1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD 48.0 MPa
6960 psi
ASTM D882
Film Tensile Strength at Break, TD 31.0 MPa
4500 psi
ASTM D882
Processing Properties Metric English Comments
Melt Temperature 221 °C
430 °F