Chevron Phillips Dynex™ D604D6 Enhanced LLDPE Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips Dynex™ D604D6 Enhanced LLDPE Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: enhanced linear low density polyethylene, slip, antiblock and processing aid additivesCharacteristics: superior dart impact, optical, hot-tack and heat seal properties, good drawdown, can be used straight or blended with LDPE or HDPEApplications: thick or thin film applications where superior toughness and abuse resistance, hot-tack and heat-seal, and optical properties are criticalNatural ColorSlip: 1500 ppmAntiblock: 7000 ppm.Recommended processing conditions: 6.35 cm extruder. 24:1 screw L/D ratio. 0.203 cm die opening. Melt temperature 232°C. Blow up ratio 2.5:1. Output rate 8.0 lb/hr/in die cir.Hot-Tack Initiation Temperature: 86°CUltimate Hot-Tack Strength: 3.8 NHeat Seal Initiation Temperature at 0.5 lb.: 96°CUltimate Heat Seal Strength: 13.6 N.Film properties based on thickness of 0.0318 mm.Information provided by Chevron Phillips Chemical Company.
Physical Properties Metric English Comments
Density 0.917 g/cc
0.0331 lb/in³
ASTM D4883
Melt Flow 0.40 g/10 min
0.40 g/10 min
Condition E; ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 550 %
550 %
ASTM D882
Film Elongation at Break, TD 690 %
690 %
ASTM D882
Secant Modulus, MD 0.180 GPa
26.1 ksi
ASTM D882
Secant Modulus, TD 0.190 GPa
27.6 ksi
ASTM D882
Coefficient of Friction 0.10
0.10
ASTM D1894
Elmendorf Tear Strength, MD 20.9 g/micron
530 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 31.1 g/micron
790 g/mil
ASTM D1922
Dart Drop 40.3 g/micron
1020 g/mil
F-50 at 26 in.; ASTM D1709
Dart Drop Test 1280 g
2.82 lb
F-50 at 26 in.; ASTM D1709
Film Tensile Strength at Break, MD 52.0 MPa
7540 psi
ASTM D882
Film Tensile Strength at Break, TD 41.2 MPa
5980 psi
ASTM D882
Optical Properties Metric English Comments
Haze 14 %
14 %
ASTM D2457
Gloss 54 %
54 %
45°. ASTM D 2457
87 %
87 %
60°, ASTM D 2457
Processing Properties Metric English Comments
Melt Temperature 232 °C
450 °F