Chevron Phillips 7120ST LLDPE Blown Film Resin, Hexene Copolymer  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips 7120ST LLDPE Blown Film Resin, Hexene Copolymer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: Hexene Copolymer, Cast/Blown Film ResinCharacteristics: Good Drawdown, Can be used in blown or cast applicationsApplications:Stretch Wrap, CoextrusionsProcessing Conditions: Extruder 6.35 cm. Screw L/D Ratio 24:1. Die Opening 0.064 cm.Film properties below based on film thickness of 20 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D1505
Melt Flow 2.0 g/10 min
2.0 g/10 min
Condition E; ASTM D 1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 550 %
550 %
ASTM D882
Film Elongation at Break, TD 850 %
850 %
ASTM D882
Secant Modulus, MD 0.130 GPa
18.9 ksi
ASTM D882
Secant Modulus, TD 0.130 GPa
18.9 ksi
ASTM D882
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ASTM D882
Film Tensile Strength at Break, TD 50.0 MPa
7250 psi
ASTM D882
Optical Properties Metric English Comments
Haze 2.0 %
2.0 %
ASTM D2457
Gloss 90 %
90 %
at 45°. ASTM D 2457
150 %
150 %
at 60°. ASTM D 2457
Processing Properties Metric English Comments
Melt Temperature 270 °C
518 °F