Chemours Viton® A-200 with Ti-Pure R960 Fluoroelastomer Compound

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Chemours
Trade Name Viton®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chemours Viton® A-200 with Ti-Pure R960 Fluoroelastomer Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lower viscosity Improved mold flow Excellent extrusion characteristics Better mold release Less mold fouling Improved compression set resistance Applications Transfer and injection molding for O-rings, Valve stem seals and shaft seals, and Parts with complicated shapes Extrusions for Fuel hose and tubing Solution coating for Fabric and Tanks or chemical containers Chemours was formed from former DuPont performance chemicals businesses, including the Viton product line, in 2015.
Mechanical Properties Metric English Comments
Hardness, Shore A 61
61
24 hours Postcure; ASTM D2240
Tensile Strength at Break 10.7 MPa
1550 psi
24 hours Postcure; ASTM D412
Elongation at Break 270 %
270 %
24 hours Postcure; ASTM D412
100% Modulus 0.00290 GPa
0.421 ksi
24 hours Postcure; ASTM D412
Compression Set 12 %

@Temperature 23.0 °C,
Time 252000 sec
12 %

@Temperature 73.4 °F,
Time 70.0 hour
O-Rings; ASTM D395B
14 %

@Temperature 200 °C,
Time 252000 sec
14 %

@Temperature 392 °F,
Time 70.0 hour
O-Rings; ASTM D395B
18 %

@Temperature 232 °C,
Time 79200 sec
18 %

@Temperature 450 °F,
Time 22.0 hour
O-Rings; ASTM D395B
34 %

@Temperature 200 °C,
Time 1.21e+6 sec
34 %

@Temperature 392 °F,
Time 336 hour
O-Rings; ASTM D395B
Processing Properties Metric English Comments
Processing Temperature 180 °C

@Time 601 sec
356 °F

@Time 0.167 hour
Press Cure
232 °C

@Time 86400 sec
450 °F

@Time 24.0 hour
Postcure
Descriptive Properties Value Comments
Formulation as Tested 0.5
VPA No.1
0.5
VPA No.3
2.2
Viton® Curative #50
3
MgO
30
Ti-Pure R960
6
Ca(OH)2
97.8
A-200