Chase Plastics CP Pryme® PPC100-20M Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® PPC100-20M Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 18.6 MPa | 2700 psi | ASTM D638 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D638 |
| Flexural Strength | 31.0 MPa | 4500 psi | ASTM D790 |
| Flexural Modulus | 0.862 GPa | 125 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 °C | 170 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Quadrant EPP Ertalon® LFX PA 6 + oil, cast (ISO Data)
- SABIC Innovative Plastics Lexan® 923ASR PC
- Resirene Resirene® 2220 Medium Impact Polystyrene
- Hybrid Plastics Nanoreinforced® POSS® Polyimide
- Universal Wire Works No. 21 Cobalt Alloy Welding Wire
- Westlake EMAC® SP2202 21.5% Ethylene-Methyl Acrylate Copolymer
- Hippe PF CP 31 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod
- Polykemi AB POLYfill PPC T1020 Polypropylene Copolymer, Mineral Reinforced
- 3M OFL0109 Outdoor UL Recognized Lexan Label Products
Copyright © lookpolymers.com All Rights Reserved