Chase Plastics CP Pryme® NNN260L (Dry) Nylon 66/6 Copolymer, 60% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 60% Glass Fiber Reinforced
Manufacturer	Chase Plastics
Trade Name	CP Pryme®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chase Plastics CP Pryme® NNN260L (Dry) Nylon 66/6 Copolymer, 60% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Good chemical resistanceGood compressive strengthGood creep resistanceGood dimensional stabilityGood flowGrease resistantOil resistantHigh rigiditySolvent resistantHigh tensile strengthHigh thermal stabilityGood toughnessForm: PelletsApplications: Automotive under the hoodInformation provided by Chase Plastics.

Physical Properties	Metric	English	Comments
Density	1.70 g/cc	0.0614 lb/in³	ASTM D792
Filler Content	60 %	60 %
Water Absorption	0.40 %	0.40 %	At 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	0.125 in; ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	269 MPa	39000 psi	ASTM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Flexural Strength	400 MPa	58000 psi	ASTM D790
Flexural Modulus	16.5 GPa	2400 ksi	ASTM D790
Izod Impact, Notched	1.66 J/cm	3.10 ft-lb/in	0.125 in; ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	238 °C	461 °F
Deflection Temperature at 1.8 MPa (264 psi)	230 °C	446 °F	Unannealed; ASTM D648