Chase Plastics CP Pryme® A100HF ABS Molding Resin, High Flow
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® A100HF ABS Molding Resin, High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 45 g/10 min @Load 10.0 kg, Temperature 220 °C |
45 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7100 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Strength | 79.3 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 2.59 GPa | 375 ksi | ASTM D790 |
| Izod Impact, Notched | 1.71 J/cm | 3.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C @Thickness 3.17 mm |
200 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C @Thickness 3.17 mm |
190 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® FG 23 I Butene Copolymer Linear Low Density Polyethylene
- LG Chemical AF360C ABS, TBBA-free Flame Retardant, High Flow
- Skamol Group Moler M-EXTRA 'E' Insulating Block
- Diamond Polymers ABS 7600B
- Dow AFFINITY™ EG 8200 Polyolefin Elastomer
- DuPont Teijin Films Mylar® MC2 Polyester Film, 50 Gauge (14 µm), PVDC Coated
- NOVA Chemicals Sclair® 35BPM MDPE Extrusion Resin, 2.2% Carbon Black Filled (discontinued **)
- ExxonMobil Paxon™ BA7718 Sheet Extrusion and Blow Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved