Chase Plastics CP Pryme® A100 ABS Molding Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® A100 ABS Molding Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7100 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 76.5 MPa | 11100 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm | 6.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.1 °C @Thickness 3.17 mm |
205 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.6 °C @Thickness 3.17 mm |
195 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |