Celanese Zenite® FG6330 NC011 LCP

Category	Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), Mineral Filled
Manufacturer	Celanese Corporation
Trade Name	Zenite®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Celanese Zenite® FG6330 NC011 LCP.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Zenite® FG6330 NC011 is a 30% mineral reinforced liquid crystal polymer resin with FDA approval for use in repeated food-contact applications.Celenese acquired the Zenite product line from DuPont in 2010.

Physical Properties	Metric	English	Comments
Density	1.64 g/cc	0.0592 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.00 cm/cm @Thickness 2.00 mm	0.00 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0065 cm/cm @Thickness 2.00 mm	0.0065 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	130 MPa	18900 psi	ISO 527
Elongation at Break	5.0 %	5.0 %	ISO 527
Tensile Modulus	10.0 GPa	1450 ksi	ISO 527
Flexural Strength	145 MPa @Temperature 23.0 °C	21000 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	7.10 GPa @Temperature 23.0 °C	1030 ksi @Temperature 73.4 °F	ISO 178
Charpy Impact, Notched	0.900 J/cm² @Temperature 23.0 °C	4.28 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	335 °C	635 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	245 °C	473 °F	ISO 75-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	355 °C	671 °F	Optimum
	350 - 360 °C	662 - 680 °F
Mold Temperature	80.0 °C	176 °F	Optimum
	40.0 - 150 °C	104 - 302 °F
Drying Temperature	150 °C	302 °F
Dry Time	3 hour	3 hour	Dehumidified Dryer
Moisture Content	<= 0.010 %	<= 0.010 %

Descriptive Properties	Value	Comments
Color	Natural
Drying Recommended	Yes
Forms	Pellets
Generic	LCP
Part Marking Code	>LCP-MD30<	ISO 11469
Product Category	Food Contact Resins
	Mineral Reinforced Resins
Region Available	Americas
	Asia/Pacific
	Europe
Resin Identification	LCP-MD30	ISO 1043