Celanese Zenite® 6140L BK010 LCP

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name Zenite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Zenite® 6140L BK010 LCP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zenite® 6140L BK010 is a 40% glass reinforced, lubricated, black liquid crystal polymer resin with high stiffness and a heat deflection temperature of 280°C.Celenese acquired the Zenite product line from DuPont in 2010.
Physical Properties Metric English Comments
Specific Gravity 1.71 g/cc
1.71 g/cc
ASTM D 792
Density 1.71 g/cc
0.0618 lb/in³
ISO 1183
Filler Content 40 %
40 %
Linear Mold Shrinkage, Flow 0.00050 cm/cm

@Thickness 2.00 mm
0.00050 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 cm/cm

@Thickness 2.00 mm
0.0050 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
ISO 527
Tensile Strength, Ultimate 135 MPa

@Thickness 3.17 mm,
Temperature 23.0 °C
19600 psi

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D638
Elongation at Break 1.1 %
1.1 %
ISO 527
1.3 %

@Thickness 3.17 mm,
Temperature 23.0 °C
1.3 %

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D638
Tensile Modulus 17.0 GPa

@Temperature 23.0 °C
2470 ksi

@Temperature 73.4 °F
ISO 527
Flexural Strength 190 MPa

@Temperature 23.0 °C
27600 psi

@Temperature 73.4 °F
ISO 178
183 MPa

@Thickness 3.17 mm,
Temperature 23.0 °C
26500 psi

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D790
Flexural Modulus 16.5 GPa

@Temperature 23.0 °C
2390 ksi

@Temperature 73.4 °F
ISO 178
15.6 GPa

@Thickness 3.17 mm,
Temperature 23.0 °C
2260 ksi

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D790
Izod Impact, Notched 1.12 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
2.10 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D256
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO) 20.0 kJ/m²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1U
20.0 kJ/m²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
2.30 J/cm²

@Temperature 23.0 °C
10.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 0.000 µm/m-°C

@Thickness 2.00 mm,
Temperature 160 - 260 °C
0.000 µin/in-°F

@Thickness 0.0787 in,
Temperature 320 - 500 °F
ISO 11359-1/-2
2.00 µm/m-°C

@Thickness 4.00 mm,
Temperature 160 - 260 °C
1.11 µin/in-°F

@Thickness 0.157 in,
Temperature 320 - 500 °F
ISO 11359-1/-2
3.00 µm/m-°C

@Thickness 4.00 mm,
Temperature -40.0 - 23.0 °C
1.67 µin/in-°F

@Thickness 0.157 in,
Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
3.00 µm/m-°C

@Thickness 2.00 mm,
Temperature -40.0 - 23.0 °C
1.67 µin/in-°F

@Thickness 0.0787 in,
Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
3.00 µm/m-°C

@Thickness 2.00 mm,
Temperature -40.0 - 260 °C
1.67 µin/in-°F

@Thickness 0.0787 in,
Temperature -40.0 - 500 °F
ISO 11359-1/-2
3.00 µm/m-°C

@Thickness 4.00 mm,
Temperature -40.0 - 260 °C
1.67 µin/in-°F

@Thickness 0.157 in,
Temperature -40.0 - 500 °F
ISO 11359-1/-2
3.00 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
1.67 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-1/-2
3.00 µm/m-°C

@Thickness 2.00 mm,
Temperature 55.0 - 160 °C
1.67 µin/in-°F

@Thickness 0.0787 in,
Temperature 131 - 320 °F
ISO 11359-1/-2
4.00 µm/m-°C

@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C
2.22 µin/in-°F

@Thickness 0.157 in,
Temperature 73.4 - 131 °F
ISO 11359-1/-2
5.00 µm/m-°C

@Thickness 4.00 mm,
Temperature 55.0 - 160 °C
2.78 µin/in-°F

@Thickness 0.157 in,
Temperature 131 - 320 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 55.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2; 2mm
56.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
31.1 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2; 4mm
77.0 µm/m-°C

@Temperature -40.0 - 260 °C
42.8 µin/in-°F

@Temperature -40.0 - 500 °F
ISO 11359-1/-2; 2mm
79.0 µm/m-°C

@Temperature -40.0 - 260 °C
43.9 µin/in-°F

@Temperature -40.0 - 500 °F
ISO 11359-1/-2; 4mm
62.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
34.4 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-1/-2
64.0 µm/m-°C

@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C
35.6 µin/in-°F

@Thickness 0.157 in,
Temperature 73.4 - 131 °F
ISO 11359-1/-2
80.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 55.0 - 160 °C
44.4 µin/in-°F

@Thickness 0.0787 in,
Temperature 131 - 320 °F
ISO 11359-1/-2
82.0 µm/m-°C

@Thickness 4.00 mm,
Temperature 55.0 - 160 °C
45.6 µin/in-°F

@Thickness 0.157 in,
Temperature 131 - 320 °F
ISO 11359-1/-2
90.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 160 - 260 °C
50.0 µin/in-°F

@Thickness 0.0787 in,
Temperature 320 - 500 °F
ISO 11359-1/-2
94.0 µm/m-°C

@Thickness 4.00 mm,
Temperature 160 - 260 °C
52.2 µin/in-°F

@Thickness 0.157 in,
Temperature 320 - 500 °F
ISO 11359-1/-2
Melting Point 335 °C
635 °F
ASTM D 3418
335 °C
635 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 271 °C
520 °F
ASTM D 648
280 °C
536 °F
ISO 75-1/-2
Glass Transition Temp, Tg 120 °C
248 °F
ASTM D 3418
UL RTI, Electrical 240 °C

@Thickness 1.50 mm
464 °F

@Thickness 0.0591 in
UL 746B
240 °C

@Thickness 0.750 mm
464 °F

@Thickness 0.0295 in
UL 746B
240 °C

@Thickness 3.00 mm
464 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical with Impact 220 °C

@Thickness 1.50 mm
428 °F

@Thickness 0.0591 in
UL 746B
220 °C

@Thickness 0.750 mm
428 °F

@Thickness 0.0295 in
UL 746B
220 °C

@Thickness 3.00 mm
428 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical without Impact 240 °C

@Thickness 1.50 mm
464 °F

@Thickness 0.0591 in
UL 746B
240 °C

@Thickness 0.750 mm
464 °F

@Thickness 0.0295 in
UL 746B
240 °C

@Thickness 3.00 mm
464 °F

@Thickness 0.118 in
UL 746B
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Dielectric Strength 27.0 kV/mm

@Thickness 2.00 mm
686 kV/in

@Thickness 0.0787 in
IEC 60243-1
45.0 kV/mm

@Thickness 1.00 mm
1140 kV/in

@Thickness 0.0394 in
IEC 60243-1
Comparative Tracking Index 175 V
175 V
IEC 60112
175 - 249 V
175 - 249 V
UL 746A