Celanese ZENITE ZE55311E LCP, Mineral Reinforced

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP)
Manufacturer Celanese Corporation
Trade Name ZENITE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese ZENITE ZE55311E LCP, Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zenite ZE55311E is mineral filled LCP resin with improved elongation, low abrasion and smooth surface.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.63 g/cc
0.0589 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.000500 cm/cm
0.000500 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00730 cm/cm
0.00730 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
5mm/min; ISO 527-2/1A
Elongation at Break 4.30 %
4.30 %
5mm/min; ISO 527-2/1A
Tensile Modulus 8.50 GPa
1230 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 140 MPa
20300 psi
ISO 178
Flexural Modulus 9.00 GPa
1310 ksi
ISO 178
Charpy Impact Unnotched 2.64 J/cm²
12.6 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 320 °C
608 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 258 °C
496 °F
ISO 75-1, -2
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Dielectric Constant 4.27

@Frequency 2.05e+9 Hz
4.27

@Frequency 2.05e+9 Hz
Dissipation Factor 14.0

@Frequency 2.05e+9 Hz
14.0

@Frequency 2.05e+9 Hz
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
cavity
Feed Temperature 40.0 - 60.0 °C
104 - 140 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 320 - 330 °C
608 - 626 °F
Zone 2 335 - 345 °C
635 - 653 °F
Zone 3 335 - 345 °C
635 - 653 °F
Zone 4 335 - 345 °C
635 - 653 °F
Die Temperature 335 - 345 °C
635 - 653 °F
Melt Temperature 325 - 345 °C
617 - 653 °F
Drying Temperature >= 150 °C
>= 302 °F
Dry Time 3.00 hour
3.00 hour
Moisture Content <= 0.0100 %
<= 0.0100 %
Injection Pressure 50.0 - 150 MPa
7250 - 21800 psi
Hold Pressure 50.0 - 150 MPa
7250 - 21800 psi
Back Pressure <= 3.00 MPa
<= 435 psi