Celanese ZENITE ZE16401 LCP, 30% Specialty

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name ZENITE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese ZENITE ZE16401 LCP, 30% Specialty.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zenite« ZE16401 is a 30% mineral reinforced and Teflon« PTFE powder filled liquid crystal polymer for injection molding. and It is well suited for low wear / low friction applications.Information provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 1.67 g/cc
0.0603 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
5mm/min; ISO 527-2/1A
Elongation at Break 3.8 %
3.8 %
5mm/min; ISO 527-2/1A
Tensile Modulus 8.50 GPa
1230 ksi
1mm/min; ISO 527-2/1A
Flexural Strength 135 MPa
19600 psi
ISO 178
Flexural Modulus 6.60 GPa
957 ksi
ISO 178
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 335 °C
635 °F
ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
ISO 75-1, -2
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Processing Properties Metric English Comments
Processing Temperature 40.0 - 150 °C
104 - 302 °F
cavity
Melt Temperature 350 - 360 °C
662 - 680 °F
Drying Temperature >= 150 °C
>= 302 °F
Dry Time 3 hour
3 hour
Moisture Content 0.010 %
0.010 %
Necessary low maximum