Celanese ZENITE 7130 LCP, 30% Glass Reinforced

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name ZENITE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese ZENITE 7130 LCP, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zenite« 7130 is a 30% glass fiber reinforced liquid crystal polymer for injection molding. It has excellent impact resistance and excellent heat deflection temperature.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.000100 cm/cm
0.000100 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00600 cm/cm
0.00600 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.50 %
1.50 %
5mm/min; ISO 527-2/1A
Tensile Modulus 17.0 GPa
2470 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 210 MPa
30500 psi
ISO 178
Flexural Modulus 13.0 GPa
1890 ksi
ISO 178
Izod Impact, Notched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
ISO 180/1A
30.0 kJ/m²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
ISO 179/1eU
2.20 J/cm²

@Temperature -30.0 °C
10.5 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179/1eA
2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 3.00 µm/m-°C
1.67 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 62.0 µm/m-°C
34.4 µin/in-°F
ISO 11359-2
Melting Point 352 °C
666 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 310 °C
590 °F
ISO 75-1, -2
Glass Transition Temp, Tg 120 °C
248 °F
ISO 11357-1,-2,-3
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
Oxygen Index 45.0 %
45.0 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.70

@Frequency 1.00e+6 Hz
3.70

@Frequency 1.00e+6 Hz
IEC 60250
4.10

@Frequency 100 Hz
4.10

@Frequency 100 Hz
IEC 60250
Dielectric Strength 45.0 kV/mm
1140 kV/in
IEC 60243-1
Dissipation Factor 0.0140

@Frequency 100 Hz
0.0140

@Frequency 100 Hz
IEC 60250
0.0300

@Frequency 1.00e+6 Hz
0.0300

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 175 V
175 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
cavity
Feed Temperature 40.0 - 60.0 °C
104 - 140 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 355 - 365 °C
671 - 689 °F
Zone 2 360 - 370 °C
680 - 698 °F
Zone 3 360 - 370 °C
680 - 698 °F
Zone 4 360 - 370 °C
680 - 698 °F
Die Temperature 360 - 370 °C
680 - 698 °F
Melt Temperature 360 - 370 °C
680 - 698 °F
Drying Temperature >= 150 °C
>= 302 °F
Dry Time 3.00 hour
3.00 hour
Moisture Content <= 0.0100 %
<= 0.0100 %
Injection Pressure 50.0 - 150 MPa
7250 - 21800 psi
Hold Pressure 50.0 - 150 MPa
7250 - 21800 psi
Back Pressure <= 3.00 MPa
<= 435 psi