Celanese ZENITE 6244L LCP, 40% Mineral / Glass Reinforced

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name ZENITE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese ZENITE 6244L LCP, 40% Mineral / Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zenite 6244L is a lubricated, 40% glass fiber and mineral reinforced liqud crystal polymer resin. It is well suited for use in the automotive, electrical/electronic, telecommunications, and aerospace industries.Information provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 1.73 g/cc
0.0625 lb/in³
ISO 1183
Water Absorption at Saturation 0.020 %
0.020 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 112 MPa
16200 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.5 %
1.5 %
5mm/min; ISO 527-2/1A
Tensile Modulus 13.1 GPa
1900 ksi
1mm/min; ISO 527-2/1A
Flexural Strength 163 MPa
23600 psi
ISO 178
Flexural Modulus 13.2 GPa
1910 ksi
ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 20.0 kJ/m²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 6.00 µm/m-°C
3.33 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C
27.8 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 269 °C
516 °F
ISO 75-1, -2
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
IEC 60250
4.4

@Frequency 100 Hz
4.4

@Frequency 100 Hz
IEC 60250
Dielectric Strength 34.0 kV/mm
864 kV/in
IEC 60243-1
Dissipation Factor 0.013

@Frequency 100 Hz
0.013

@Frequency 100 Hz
IEC 60250
0.023

@Frequency 1.00e+6 Hz
0.023

@Frequency 1.00e+6 Hz
IEC 60250
Processing Properties Metric English Comments
Processing Temperature 40.0 - 150 °C
104 - 302 °F
cavity
Melt Temperature 350 - 360 °C
662 - 680 °F
Drying Temperature 150 °C
302 °F
Dry Time 3 hour
3 hour
Moisture Content 0.010 %
0.010 %
Necessary low maximum