- Celanese ZENITE 5115L LCP, 15% Glass Reinforced (Unverified Data**)
Celanese ZENITE 5115L LCP, 15% Glass Reinforced (Unverified Data**)
| Category | Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 20% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Celanese ZENITE 5115L LCP, 15% Glass Reinforced
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zenite® 5115L is a 15% glass fiber reinforced liquid crystal polymer for injection molding with improved toughness.15% glass-reinforced, lubricatedInformation provided by Celanese
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.3 % | 3.3 % | 5mm/min; ISO 527-2/1A |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 319 °C | 606 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.5 @Frequency 1.00e+6 Hz |
2.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.76 @Frequency 2.05e+9 Hz |
3.76 @Frequency 2.05e+9 Hz |
IPC TM-650 2.5.5.13 | |
| Dissipation Factor | 0.0030 @Frequency 2.05e+9 Hz |
0.0030 @Frequency 2.05e+9 Hz |
IPC TM-650 2.5.5.13 |
| 0.0159 @Frequency 1.00e+6 Hz |
0.0159 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |
| Feed Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Zone 1 | 320 - 330 °C | 608 - 626 °F | |
| Zone 2 | 335 - 345 °C | 635 - 653 °F | |
| Zone 3 | 335 - 345 °C | 635 - 653 °F | |
| Zone 4 | 335 - 345 °C | 635 - 653 °F | |
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |
| Melt Temperature | 325 - 345 °C | 617 - 653 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Moisture Content | 0.010 % | 0.010 % | Necessary low maximum residual |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Back Pressure | 3.00 MPa | 435 psi |
Users viewing this material also viewed the following:
- MV Labs RB700 RbNO3 Rubidium nitrate
- ExxonMobil Escorene® LL-3218 LLDPE/Hexene Premium Cast Stretch Film Resin, 1.2 mil (discontinued **)
- Eastman 5274 LDPE 4% VA Copolymer, High Clarity, High Impact Film Resin (discontinued **)
- ITW Plexus Plexusâ„¢ MA3940 Methacrylate Adhesive
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC (Asia Pacific)
- Silberline Silvet® 430-30-E1
- Entec Hypel® PEHD20/.953 HDPE
- AK Steel 11 Cr-Cb™ Ferritic Stainless steel
- BASF Pluracol® 355 Specialty Polyol
- Pau Tai UNINOX PA-551 PVC Processing Aid
Copyright © lookpolymers.com All Rights Reserved