Celanese Vectra® A410 Liquid Crystal Polymer (LCP), 25% Glass/25% Mineral Filled

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), Mineral Filled
Manufacturer Celanese Corporation
Trade Name Vectra®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Vectra® A410 Liquid Crystal Polymer (LCP), 25% Glass/25% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 1.84 g/cc
0.0665 lb/in³
ISO 1183
Water Absorption 0.040 %
0.040 %
Immersion to equilibrium; ISO 62
Moisture Absorption at Equilibrium 0.040 %
0.040 %
ISO 62
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
0.0030 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 76
76
ISO 2039-2
Tensile Strength, Ultimate 150 MPa
21800 psi
ISO 527
Elongation at Break 2.0 %
2.0 %
IEC 527
Tensile Modulus 20.0 GPa
2900 ksi
ISO 527
Flexural Strength 220 MPa
31900 psi
ISO 178
Flexural Modulus 18.0 GPa
2610 ksi
ISO 178
Compressive Strength 116 MPa
16800 psi
1% Deflection, ISO 604
Compressive Modulus 19.0 GPa
2760 ksi
ISO 604
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO 180/1A
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179
Coefficient of Friction, Dynamic 0.21
0.21
vs. steel; ASTM D1984
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 5.00 µm/m-°C

@Temperature -50.0 - 200 °C
2.78 µin/in-°F

@Temperature -58.0 - 392 °F
5.00 µm/m-°C

@Temperature -58.0 - 390 °C
2.78 µin/in-°F

@Temperature -72.4 - 734 °F
CTE, linear, Transverse to Flow 66.0 µm/m-°C

@Temperature -50.0 - 200 °C
36.7 µin/in-°F

@Temperature -58.0 - 392 °F
66.0 µm/m-°C

@Temperature -50.0 - 200 °C
36.7 µin/in-°F

@Temperature -58.0 - 392 °F
Melting Point 280 °C
536 °F
ISO 3146
Maximum Service Temperature, Air 130 °C
266 °F
Generic Rating for Vectra LCP
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
ISO 75/A
Vicat Softening Point 235 °C
455 °F
ASTM D1525
UL RTI, Electrical 130 °C
266 °F
Generic Rating for Vectra LCP
UL RTI, Mechanical with Impact 130 °C
266 °F
Generic Rating for Vectra LCP
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 93
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 93
Dielectric Constant 3.9

@Frequency 1e+7 Hz
3.9

@Frequency 1e+7 Hz
4.4

@Frequency 1000 Hz
4.4

@Frequency 1000 Hz
IEC 250
Dissipation Factor 0.0070

@Frequency 1e+7 Hz
0.0070

@Frequency 1e+7 Hz
0.020

@Frequency 1000 Hz
0.020

@Frequency 1000 Hz
IEC 250
Arc Resistance 180 sec
180 sec
Comparative Tracking Index 175 V
175 V
IEC 112