Celanese VECTRA MT4310 LCP, 30% Medical Technology

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name VECTRA
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese VECTRA MT4310 LCP, 30% Medical Technology.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Highest temperature capability, easiest flow. Suitable where very thin walls are required. Used for broad range of SMT applications, with minimal dimensional change. 30% glass filled.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.61 g/cc
0.0582 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.00100 cm/cm
0.00100 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00500 cm/cm
0.00500 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 71.0
71.0
ISO 2039-2
Tensile Strength at Break 150 MPa
21800 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.60 %
1.60 %
5mm/min; ISO 527-2/1A
Tensile Modulus 15.0 GPa
2180 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 225 MPa
32600 psi
ISO 178
Flexural Modulus 15.0 GPa
2180 ksi
ISO 178
Compressive Strength 93.0 MPa

@Strain 1.00 %
13500 psi

@Strain 1.00 %
ISO 604
Compressive Modulus 14.0 GPa
2030 ksi
ISO 604
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
ISO 180/1A
31.0 kJ/m²

@Temperature 23.0 °C
14.8 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 4.30 J/cm²
20.5 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 2.20 J/cm²
10.5 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 7.00 µm/m-°C
3.89 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 20.0 µm/m-°C
11.1 µin/in-°F
ISO 11359-2
Melting Point 335 °C
635 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 276 °C
529 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 216 °C
421 °F
ISO 75-1, -2
Vicat Softening Point 195 °C
383 °F
ISO 306
Flammability, UL94 V-0
V-0
Oxygen Index 45.0 %
45.0 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 3.30

@Frequency 1.00e+6 Hz
3.30

@Frequency 1.00e+6 Hz
IEC 60250
4.00

@Frequency 100 Hz
4.00

@Frequency 100 Hz
IEC 60250
Dielectric Strength 32.0 kV/mm
813 kV/in
IEC 60243-1
Dissipation Factor 0.0100

@Frequency 100 Hz
0.0100

@Frequency 100 Hz
IEC 60250
0.0250

@Frequency 1.00e+6 Hz
0.0250

@Frequency 1.00e+6 Hz
IEC 60250
Arc Resistance 140 sec
140 sec
Internal
Comparative Tracking Index 200 V
200 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
cavity
335 - 345 °C
635 - 653 °F
hot runner
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 315 - 325 °C
599 - 617 °F
Zone 2 320 - 330 °C
608 - 626 °F
Zone 3 325 - 335 °C
617 - 635 °F
Zone 4 330 - 340 °C
626 - 644 °F
Die Temperature 335 - 345 °C
635 - 653 °F
Melt Temperature 340 °C
644 °F
ISO 294
335 - 345 °C
635 - 653 °F
Mold Temperature 100 °C
212 °F
ISO 294
Injection Velocity 150 mm/sec
5.91 in/sec
ISO 294
Drying Temperature >= 170 °C
>= 338 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content <= 0.0100 %
<= 0.0100 %
Injection Pressure 50.0 - 150 MPa
7250 - 21800 psi
Hold Pressure 69.0 MPa
10000 psi
ISO 294
50.0 - 150 MPa
7250 - 21800 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 80.0 rpm

@Diameter 40.0 mm
80.0 rpm

@Diameter 1.57 in
140 rpm

@Diameter 25.0 mm
140 rpm

@Diameter 0.984 in
200 rpm

@Diameter 16.0 mm
200 rpm

@Diameter 0.630 in
Descriptive Properties Value Comments
Injection molding Yes