Celanese VECTRA® D130M High Flow Liquid Crystal Polymer (LCP)

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name Vectra®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese VECTRA® D130M High Flow Liquid Crystal Polymer (LCP).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Very high flow LCP suitable for encapsulation. 30% milled glassInformation provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 1.63 g/cc
0.0589 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 65
65
ISO 2039-2
Tensile Strength at Break 92.0 MPa
13300 psi
5 mm/min; ISO 527-2/1A
Elongation at Break 1.5 %
1.5 %
5 mm/min; ISO 527-2/1A
Tensile Modulus 9.50 GPa
1380 ksi
1 mm/min; ISO 527-2/1A
Flexural Strength 124 MPa
18000 psi
ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 12.0 µm/m-°C

@Temperature 20.0 °C
6.67 µin/in-°F

@Temperature 68.0 °F
ISO 11359-2
CTE, linear, Transverse to Flow 38.0 µm/m-°C

@Temperature 20.0 °C
21.1 µin/in-°F

@Temperature 68.0 °F
ISO 11359-2
Melting Point 330 °C
626 °F
ISO 11357-1,2,3
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
ISO 75-1, -2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 3.9

@Frequency 1e+6 Hz
3.9

@Frequency 1e+6 Hz
IEC 60250
4.4

@Frequency 100 Hz
4.4

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0132

@Frequency 100 Hz
0.0132

@Frequency 100 Hz
IEC 60250
0.022

@Frequency 1e+6 Hz
0.022

@Frequency 1e+6 Hz
IEC 60250
Processing Properties Metric English Comments
Rear Barrel Temperature 290 - 300 °C
554 - 572 °F
Middle Barrel Temperature 310 - 320 °C
590 - 608 °F
Front Barrel Temperature 320 - 330 °C
608 - 626 °F
Nozzle Temperature 300 - 330 °C
572 - 626 °F
Melt Temperature 320 - 340 °C
608 - 644 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F