Celanese VECTRA B230 LCP, 30% Specialty

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name VECTRA
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese VECTRA B230 LCP, 30% Specialty.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Exceptional strength and stiffness. Suitable for metal replacement applications. Electrically conductive. 30% carbon fiber reinforced.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.000 cm/cm
0.000 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00100 cm/cm
0.00100 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 99.0
99.0
ISO 2039-2
Tensile Strength at Break 200 MPa
29000 psi
5mm/min; ISO 527-2/1A
Elongation at Break 0.700 %
0.700 %
5mm/min; ISO 527-2/1A
Tensile Modulus 31.8 GPa
4610 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 300 MPa
43500 psi
ISO 178
Flexural Modulus 25.5 GPa
3700 ksi
ISO 178
Compressive Strength 204 MPa

@Strain 1.00 %
29600 psi

@Strain 1.00 %
ISO 604
Compressive Modulus 33.0 GPa
4790 ksi
ISO 604
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 1.50 J/cm²
7.14 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 1.00 µm/m-°C
0.556 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 9.00 µm/m-°C
5.00 µin/in-°F
ISO 11359-2
Melting Point 280 °C
536 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 186 °C
367 °F
ISO 75-1, -2
Vicat Softening Point 167 °C
333 °F
ISO 306
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1e+05
1e+05
IEC 60093
Surface Resistance 100 ohm
100 ohm
IEC 60093
Dielectric Constant 32.0

@Frequency 1.00e+6 Hz
32.0

@Frequency 1.00e+6 Hz
IEC 60250
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
cavity
285 - 295 °C
545 - 563 °F
hot runner
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 270 - 280 °C
518 - 536 °F
Zone 2 275 - 285 °C
527 - 545 °F
Zone 3 280 - 290 °C
536 - 554 °F
Zone 4 285 - 295 °C
545 - 563 °F
Die Temperature 290 - 300 °C
554 - 572 °F
Melt Temperature 285 - 300 °C
545 - 572 °F
304 °C
579 °F
ISO 294
Mold Temperature 100 °C
212 °F
ISO 294
Injection Velocity 150 mm/sec
5.91 in/sec
ISO 294
Drying Temperature >= 150 °C
>= 302 °F
Dry Time 6.00 - 8.00 hour
6.00 - 8.00 hour
Moisture Content <= 0.0100 %
<= 0.0100 %
Injection Pressure 50.0 - 150 MPa
7250 - 21800 psi
Hold Pressure 69.0 MPa
10000 psi
ISO 294
50.0 - 150 MPa
7250 - 21800 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 80.0 rpm

@Diameter 40.0 mm
80.0 rpm

@Diameter 1.57 in
140 rpm

@Diameter 25.0 mm
140 rpm

@Diameter 0.984 in
200 rpm

@Diameter 16.0 mm
200 rpm

@Diameter 0.630 in
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed very fast