Celanese Thermx® CG943 BK010 PCT

Category Polymer , Thermoplastic , Polyester, TP , Polycyclohexylenedimethylene Terephthalate (PCT)
Manufacturer Celanese Corporation
Trade Name Thermx®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Thermx® CG943 BK010 PCT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Thermx® CG943 BK010 is a 40% glass fiber reinforced, flame retardant, black polycyclohexylenedimethylene terephthalate resin for injection molding.Celenese acquired the Thermx product line from DuPont in 2010.
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
ISO 1183
Filler Content 40 %
40 %
Mechanical Properties Metric English Comments
Tensile Strength at Break 111 MPa
16100 psi
ISO 527
Elongation at Break 1.16 %
1.16 %
ISO 527
Tensile Modulus 0.111 GPa

@Temperature 23.0 °C
16.1 ksi

@Temperature 73.4 °F
ISO 527
Flexural Strength 169 MPa
24500 psi
ISO 178
Flexural Modulus 12.589 GPa
1825.9 ksi
ISO 178
Izod Impact, Notched (ISO) 6.10 kJ/m²

@Temperature 23.0 °C
2.90 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 2.30 J/cm²

@Temperature 23.0 °C
10.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.650 J/cm²

@Temperature 23.0 °C
3.09 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 285 °C
545 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1/-2
UL RTI, Electrical 150 °C

@Thickness 1.50 mm
302 °F

@Thickness 0.0591 in
UL 746B
150 °C

@Thickness 3.00 mm
302 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical without Impact 140 °C

@Thickness 1.50 mm
284 °F

@Thickness 0.0591 in
UL 746B
140 °C

@Thickness 3.00 mm
284 °F

@Thickness 0.118 in
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
IEC 60695-11-10
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL94
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
IEC 60695-11-10
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
UL94
Processing Properties Metric English Comments
Melt Temperature 300 °C
572 °F
Optimum
295 - 310 °C
563 - 590 °F
Mold Temperature 100 °C
212 °F
Optimum
80.0 - 120 °C
176 - 248 °F
Drying Temperature 95.0 °C
203 °F
Dry Time 4 - 6 hour
4 - 6 hour
Dehumidified Dryer
Moisture Content <= 0.030 %
<= 0.030 %
Descriptive Properties Value Comments
Color Black
Drying Recommended Yes
Filler Glass Reinforced
Forms Pellets
Generic PCT
Part Marking Code >PCT-GF40FR(17)<
ISO 11469
Polymer Family Polyester
Polymer Type PCT
Processing Method Injection Molding
Product Category Electrical Resins
Flame Retardant Resins
Glass Reinforced Resins
Region Available Americas
Asia/Pacific
Europe
Resin Identification PCT-GF40FR(17)