Celanese Thermx® CG053 PCT, 28% Mineral / Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polycyclohexylenedimethylene Terephthalate (PCT) , Polycyclohexylenedimethylene Terephthalate (PCT), Glass/Mineral Reinforced
Manufacturer Celanese Corporation
Trade Name Thermx®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Thermx® CG053 PCT, 28% Mineral / Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Thermx® CG053 is a 28% glass/mineral reinforced polycyclohexylenedimethylene terephthalate resin.28% glass/mineral reinforcedInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 92.0 MPa
13300 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.9 %
1.9 %
5mm/min; ISO 527-2/1A
Tensile Modulus 7.50 GPa
1090 ksi
1mm/min; ISO 527-2/1A
Flexural Strength 140 MPa
20300 psi
ISO 178
Flexural Modulus 7.00 GPa
1020 ksi
ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 283 °C
541 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
Cavity temperature
Melt Temperature 295 - 310 °C
563 - 590 °F
Drying Temperature >= 95.0 °C
>= 203 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.030 %
0.030 %
Necessary low maximum residual