Celanese RITEFLEX 655HS TPC, Unfilled
| Category | Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Celanese Corporation |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Celanese RITEFLEX 655HS TPC, Unfilled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
55 Shore D Hardness heat stabilizedInformation provided by Celanese
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 0.000689 g/cc | 0.0000249 lb/in³ | ASTM D792 |
| 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 | |
| Water Absorption | 0.400 % @Temperature 22.8 °C |
0.400 % @Temperature 73.0 °F |
24hr immersion; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0100 cm/cm | 0.0100 in/in | ASTM D955 |
| 0.0160 - 0.0190 cm/cm | 0.0160 - 0.0190 in/in | ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0170 - 0.0210 cm/cm | 0.0170 - 0.0210 in/in | ISO 294-4 |
| Melt Flow | 9.00 g/10 min @Load 2.16 kg, Temperature 220 °C |
9.00 g/10 min @Load 4.76 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55.0 | 55.0 | ASTM D2240 |
| Tensile Strength at Break | 26.2 MPa | 3800 psi | ASTM D638 |
| Elongation at Break | 330 % | 330 % | ASTM D638 |
| Flexural Strength | 7.00 MPa @Strain 3.50 % |
1020 psi @Strain 3.50 % |
ISO 178 |
| Flexural Modulus | 0.205 GPa | 29.7 ksi | ISO 178 |
| 0.207 GPa | 30.0 ksi | ASTM D790 | |
| Izod Impact, Notched | 52.9 J/cm | 99.0 ft-lb/in | ASTM D256 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 6.50 J/cm² | 30.9 ft-lb/in² | partial break; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 200 °C | 392 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | ISO 75-1, -2 |
| Vicat Softening Point | 178 °C | 352 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+12 ohm-cm | 5.00e+12 ohm-cm | ASTM D257 |
| 2.00e+15 ohm-cm | 2.00e+15 ohm-cm | IEC 60093 | |
| Dielectric Constant | 4.00 @Frequency 1.00e+6 Hz |
4.00 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | short term; ASTM D149 |
| 14.0 kV/mm | 356 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0400 @Frequency 1.00e+6 Hz |
0.0400 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | >= 600 V | >= 600 V | ASTM D3638 |
| >= 600 V | >= 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 20.0 - 55.0 °C | 68.0 - 131 °F | cavity |
| 205 - 235 °C | 401 - 455 °F | hot runner | |
| Feed Temperature | 200 - 215 °C | 392 - 419 °F | |
| Middle Barrel Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Zone 1 | 200 - 215 °C | 392 - 419 °F | |
| Zone 2 | 205 - 230 °C | 401 - 446 °F | |
| Zone 3 | 205 - 230 °C | 401 - 446 °F | |
| Zone 4 | 205 - 235 °C | 401 - 455 °F | |
| Die Temperature | 205 - 235 °C | 401 - 455 °F | |
| Melt Temperature | 205 - 235 °C | 401 - 455 °F | |
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | <= 0.0500 % | <= 0.0500 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | medium-fast | |
| Processing type | Inj/Blow/Ext |
Users viewing this material also viewed the following:
- Nye Lubricants 718S (NG) Rheolube Grease
- PTS Trimid® N66-G13HL 13% Glass Fiber Reinforced Heat Stabilized, Lubed Nylon 6/6
- Albis Plastics ASA 02A 811 Unreinforced (discontinued **)
- SABIC Innovative Plastics Noryl PX7446 PPE+PS
- SolVin 250SB Polyvinyl Chloride General Purpose - Rigid
- A. Schulman PAPERMATCH® T-4448/50 Specialty Masterbatch
- Westlake Plastics Kynar® 740 PVDF Homopolymer
- Hexcel® HexPly® 922-1 180°C Curing Epoxy Matrix
- Alliance Polymers Viprene™ G75A-32U-NAT Thermoplastic Vulcanizate Elastomer
- Hexcel® HexPly® M56 180°C (350°F) Out-of-Autoclave Curing Matrix, M56/37%/280H5/AS4-3K
Copyright © lookpolymers.com All Rights Reserved