Celanese IMPET 330R PET, 30% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer Celanese Corporation
Trade Name IMPET
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese IMPET 330R PET, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Impet 330R is a 30% glass reinforced injection moldable polyester containing post consumer recycled PET. It provides an excellent combination of strength, stiffness, and high temperature resistance.Information provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.58 g/cc
1.58 g/cc
ASTM D792
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Moisture Absorption 0.160 %
0.160 %
23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow 0.00200 cm/cm
0.00200 in/in
ISO 294-4
0.00700 cm/cm
0.00700 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.00600 cm/cm
0.00600 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 122
122
ISO 2039-2
Tensile Strength at Break 159 MPa
23100 psi
5mm/min; ISO 527-2/1A
165 MPa
24000 psi
ASTM D638
Elongation at Break 2.00 %
2.00 %
ASTM D638
2.30 %
2.30 %
5mm/min; ISO 527-2/1A
Tensile Modulus 11.1 GPa
1610 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 229 MPa
33200 psi
ISO 178
245 MPa
35500 psi
ASTM D790
Flexural Modulus 9.65 GPa
1400 ksi
ASTM D790
11.0 GPa
1600 ksi
ISO 178
Izod Impact, Notched 0.801 J/cm
1.50 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 8.80 kJ/m²
4.19 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 2.70 J/cm²
12.8 ft-lb/in²
ISO 179/1eU
2.80 J/cm²

@Temperature -30.0 °C
13.3 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.850 J/cm²
4.04 ft-lb/in²
ISO 179/1eA
0.880 J/cm²

@Temperature -30.0 °C
4.19 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C
10.0 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C
38.9 µin/in-°F
ISO 11359-2
Melting Point 244 °C
471 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 240 °C
464 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 221 °C
430 °F
ISO 75-1, -2
224 °C
435 °F
ASTM D648
Glass Transition Temp, Tg 73.0 °C
163 °F
ISO 11357-1,-2,-3
Flammability, UL94 HB
HB
Oxygen Index 25.0 %
25.0 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+15 ohm-cm
3.00e+15 ohm-cm
ASTM D257
7.00e+16 ohm-cm
7.00e+16 ohm-cm
IEC 60093
Surface Resistance 3.10e+14 ohm
3.10e+14 ohm
ASTM D257
3.00e+15 ohm
3.00e+15 ohm
IEC 60093
Dielectric Constant 2.83

@Frequency 100 Hz
2.83

@Frequency 100 Hz
IEC 60250
3.10

@Frequency 10000 Hz
3.10

@Frequency 10000 Hz
ASTM D150
3.20

@Frequency 1000 Hz
3.20

@Frequency 1000 Hz
ASTM D150
3.46

@Frequency 1.00e+6 Hz
3.46

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 22.2 kV/mm
565 kV/in
short term; ASTM D149
32.0 kV/mm
813 kV/in
IEC 60243-1
Dissipation Factor 0.0100

@Frequency 1000 Hz
0.0100

@Frequency 1000 Hz
ASTM D150
0.0120

@Frequency 100 Hz
0.0120

@Frequency 100 Hz
IEC 60250
0.0140

@Frequency 1.00e+6 Hz
0.0140

@Frequency 1.00e+6 Hz
IEC 60250
0.0160

@Frequency 10000 Hz
0.0160

@Frequency 10000 Hz
ASTM D150
Arc Resistance 125 sec
125 sec
ASTM D495
Comparative Tracking Index 175 V
175 V
ASTM D3638
175 V
175 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 110 - 121 °C
230 - 250 °F
cavity
260 - 290 °C
500 - 554 °F
hot runner
Feed Temperature 255 - 265 °C
491 - 509 °F
Middle Barrel Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 255 - 265 °C
491 - 509 °F
Zone 2 260 - 275 °C
500 - 527 °F
Zone 3 260 - 275 °C
500 - 527 °F
Zone 4 265 - 280 °C
509 - 536 °F
Die Temperature 270 - 290 °C
518 - 554 °F
Melt Temperature 260 - 290 °C
500 - 554 °F
285 °C
545 °F
ISO 294
Mold Temperature 135 °C
275 °F
ISO 294
Injection Velocity 275 mm/sec
10.8 in/sec
ISO 294
Drying Temperature 130 - 140 °C
266 - 284 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.0100 %
<= 0.0100 %
Hold Pressure 60.0 MPa
8700 psi
ISO 294
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed medium-fast
Processing conditions acc. ISO 7792-2