Celanese IMPET 2700 GV1/20 PET, 20% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced
Manufacturer Celanese Corporation
Trade Name IMPET
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese IMPET 2700 GV1/20 PET, 20% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyethylene terephthalate, 20 % glass fibre reinforced, high flowability, excellent gloss, high modulusInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C/50%RH; ISO 62
Viscosity Test 50.0 cm³/g
50.0 cm³/g
ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow 0.00300 cm/cm
0.00300 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00900 cm/cm
0.00900 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 123
123
ISO 2039-2
Tensile Strength at Break 133 MPa
19300 psi
5mm/min; ISO 527-2/1A
Elongation at Break 2.00 %
2.00 %
5mm/min; ISO 527-2/1A
Tensile Modulus 8.20 GPa
1190 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 173 MPa
25100 psi
ISO 178
Flexural Modulus 8.10 GPa
1170 ksi
ISO 178
Izod Impact, Notched (ISO) 7.20 kJ/m²
3.43 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179/1eU
2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.680 J/cm²
3.24 ft-lb/in²
ISO 179/1eA
0.660 J/cm²

@Temperature -30.0 °C
3.14 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.0 µm/m-°C
12.8 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 95.0 µm/m-°C
52.8 µin/in-°F
ISO 11359-2
Melting Point 250 °C
482 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 248 °C
478 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 233 °C
451 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 80.0 °C
176 °F
ISO 75-1, -2
Vicat Softening Point 255 °C
491 °F
ISO 306
Glass Transition Temp, Tg 80.0 °C
176 °F
ISO 11357-1,-2,-3
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Oxygen Index 24.0 %
24.0 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+16 ohm-cm
3.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
IEC 60093
Dielectric Constant 4.10

@Frequency 1.00e+6 Hz
4.10

@Frequency 1.00e+6 Hz
IEC 60250
4.60

@Frequency 100 Hz
4.60

@Frequency 100 Hz
IEC 60250
Dielectric Strength 31.0 kV/mm
787 kV/in
IEC 60243-1
Dissipation Factor 0.00300

@Frequency 100 Hz
0.00300

@Frequency 100 Hz
IEC 60250
0.0190

@Frequency 1.00e+6 Hz
0.0190

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 200 V
200 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 135 - 145 °C
275 - 293 °F
cavity
270 - 290 °C
518 - 554 °F
hot runner
Feed Temperature 40.0 - 60.0 °C
104 - 140 °F
Middle Barrel Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 260 - 270 °C
500 - 518 °F
Zone 2 270 - 280 °C
518 - 536 °F
Zone 3 280 - 290 °C
536 - 554 °F
Zone 4 280 - 290 °C
536 - 554 °F
Die Temperature 270 - 290 °C
518 - 554 °F
Melt Temperature 270 - 290 °C
518 - 554 °F
Drying Temperature 120 - 140 °C
248 - 284 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Moisture Content <= 0.0100 %
<= 0.0100 %
Screw Speed 50.0 rpm

@Diameter 55.0 mm
50.0 rpm

@Diameter 2.17 in
65.0 rpm

@Diameter 40.0 mm
65.0 rpm

@Diameter 1.57 in
80.0 rpm

@Diameter 25.0 mm
80.0 rpm

@Diameter 0.984 in
Descriptive Properties Value Comments