Celanese Hostaform® UV90Z XAP2 ™ POM, UV Resistant

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer Celanese Corporation
Trade Name HOSTAFORM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Hostaform® UV90Z XAP2 ™ POM, UV Resistant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary Data SheetInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0200 cm/cm
0.0200 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0170 cm/cm
0.0170 in/in
ISO 294-4
Melt Flow 8.00 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.00 g/10 min

@Load 4.76 lb,
Temperature 374 °F
[cm3/10min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 64.0 MPa
9280 psi
50mm/min; ISO 527-2/1A
Elongation at Yield 9.00 %
9.00 %
50mm/min; ISO 527-2/1A
Tensile Modulus 2.65 GPa
384 ksi
50mm/min; ISO 527-2/1A
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-2
Melting Point 167 °C
333 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
cavity
180 - 200 °C
356 - 392 °F
hot runner
Zone 1 165 - 175 °C
329 - 347 °F
Zone 2 170 - 180 °C
338 - 356 °F
Zone 3 170 - 180 °C
338 - 356 °F
Zone 4 175 - 185 °C
347 - 365 °F
Die Temperature 180 - 190 °C
356 - 374 °F
Melt Temperature 180 - 190 °C
356 - 374 °F
Drying Temperature >= 140 °C
>= 284 °F
Dry Time 2.00 hour
2.00 hour
Injection Pressure 60.0 - 120 MPa
8700 - 17400 psi
Hold Pressure 60.0 - 120 MPa
8700 - 17400 psi
Back Pressure <= 4.00 MPa
<= 580 psi
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed slow-medium
Profile extrusion No
Sheet extrusion No