Celanese Hostaform® TF-10XAP® POM, Impact Modified  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified
Manufacturer
Trade Name Hostaform®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Hostaform® TF-10XAP® POM, Impact Modified  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hostaform® acetal copolymer TF-10 XAP® is low emission, improved flow, impact modified grade providing optimum performance in general purpose injection molding primarily for the interior automotive market. This grade provides overall excellent performImproved flow, low emission, impact modifiedInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.021 cm/cm
0.021 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
ISO 294-4
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 190 °C
13 g/10 min

@Load 4.76 lb,
Temperature 374 °F
(MVR) cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 49.0 MPa
7110 psi
50mm/min; ISO 527-2/1A
Elongation at Yield 13 %
13 %
50mm/min; ISO 527-2/1A
Tensile Modulus 1.75 GPa
254 ksi
1mm/min; ISO 527-2/1A
Flexural Modulus 1.70 GPa
247 ksi
ISO 178
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 139 °C
282 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 80.0 - 100 °C
176 - 212 °F
Cavity temperature
<= 205 °C
<= 401 °F
to avoid burning and discoloring product
Zone 1 170 - 180 °C
338 - 356 °F
Zone 2 180 - 190 °C
356 - 374 °F
Zone 3 180 - 190 °C
356 - 374 °F
Zone 4 180 - 200 °C
356 - 392 °F
Die Temperature 180 - 200 °C
356 - 392 °F
Melt Temperature 180 - 200 °C
356 - 392 °F
Drying Temperature 80.0 - 110 °C
176 - 230 °F
Dry Time 3.00 hour
3.00 hour
Injection Pressure 60.0 - 120 MPa
8700 - 17400 psi
Hold Pressure 60.0 - 120 MPa
8700 - 17400 psi
Back Pressure 0.500 MPa
72.5 psi
Hot-Working Temperature 190 - 200 °C
374 - 392 °F
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed slow-medium
Pre-drying Drying is recommended.