Celanese Hostaform® S 9364 WS 10/1570 POM, UV Resistant (Unverified Data**)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | Hostaform® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Celanese Hostaform® S 9364 WS 10/1570 POM, UV Resistant
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Preliminary Data SheetImpact modified, weatherableInformation provided by Celanese
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | ISO 62 |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
(MVR) cm³/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Yield | 20 % | 20 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 1.50 GPa | 218 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-2 |
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 60.0 - 70.0 °C | 140 - 158 °F | Cavity temperature |
| <= 205 °C | <= 401 °F | to avoid burning and discoloring product | |
| Zone 1 | 170 - 180 °C | 338 - 356 °F | |
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |
| Zone 3 | 180 - 190 °C | 356 - 374 °F | |
| Zone 4 | 180 - 200 °C | 356 - 392 °F | |
| Die Temperature | 180 - 200 °C | 356 - 392 °F | |
| Melt Temperature | 180 - 200 °C | 356 - 392 °F | |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |
| Back Pressure | 0.500 MPa | 72.5 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection molding | Yes | |
| Injection Speed | slow | |
| Pre-drying | Drying is not normally required with proper storage | |
| Processing conditions | ISO 9988-2 | |
| Profile extrusion | Yes |
Users viewing this material also viewed the following:
- Nylene® 406 Nylon 6
- Pyrotek AF-42 Low-Temperature Felt
- SABIC Innovative Plastics LNP Thermocomp 2C004
- Plenco 3557 Phenolic, Granular, Compression Molded
- Lubrizol ESTANE® GP60DE Ester Based Thermoplastic Polyurethane
- CIMBAR RMF 75 Recycled Mineral Filler
- Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (3.5 mm Molded Thickness)
- Arlon 55596R030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Ascend Performance Materials Vydyne® 49 Nylon 66, DAM
- Ashley Polymers Ashlene® P1410 Polycarbonate, 10% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved