Celanese Hostaform® S 9362 XAP² ™ POM, Impact Modified

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced, Impact Grade
Manufacturer Celanese Corporation
Trade Name HOSTAFORM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Hostaform® S 9362 XAP² ™ POM, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary Data SheetInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Water Absorption at Saturation 0.800 %
0.800 %
ISO 62
Linear Mold Shrinkage, Flow 0.0190 cm/cm
0.0190 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0180 cm/cm
0.0180 in/in
ISO 294-4
Melt Flow 6.50 g/10 min

@Load 2.16 kg,
Temperature 190 °C
6.50 g/10 min

@Load 4.76 lb,
Temperature 374 °F
[cm3/10min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
50mm/min; ISO 527-2/1A
Elongation at Yield 10.0 %
10.0 %
50mm/min; ISO 527-2/1A
Tensile Modulus 2.30 GPa
334 ksi
50mm/min; ISO 527-2/1A
Flexural Modulus 2.20 GPa
319 ksi
ISO 178
Charpy Impact Unnotched NB
NB
ISO 179/1eU
19.0 J/cm²

@Temperature -30.0 °C
90.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-2
Melting Point 166 °C
331 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
cavity
Zone 1 170 - 180 °C
338 - 356 °F
Zone 2 180 - 190 °C
356 - 374 °F
Zone 3 180 - 190 °C
356 - 374 °F
Zone 4 180 - 200 °C
356 - 392 °F
Die Temperature 180 - 200 °C
356 - 392 °F
Melt Temperature 180 - 200 °C
356 - 392 °F
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Dry Time 3.00 hour
3.00 hour
Injection Pressure 60.0 - 120 MPa
8700 - 17400 psi
Hold Pressure 60.0 - 120 MPa
8700 - 17400 psi
Back Pressure <= 2.00 MPa
<= 290 psi
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed slow
Processing conditions acc. ISO 9988-2
Profile extrusion Yes