Celanese Hostaform® S 9362 POM, Impact Modified  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified
Manufacturer
Trade Name Hostaform®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Hostaform® S 9362 POM, Impact Modified  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hostaform® acetal copolymer grade S 9362 is an impact modified grade for applications requiring improved impact. Hostaform® S 9362 provides good impact strength while improving modulus and weld line strength over standard impact modified grades such as Impact modified, improved modulus and weld lineInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4
Melt Flow 6.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
6.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
(MVR) cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
50mm/min; ISO 527-2/1A
Elongation at Yield 10 %
10 %
50mm/min; ISO 527-2/1A
Tensile Modulus 2.30 GPa
334 ksi
1mm/min; ISO 527-2/1A
Flexural Modulus 2.20 GPa
319 ksi
ISO 178
Charpy Impact Unnotched NB
NB
ISO 179/1eU
19.0 J/cm²

@Temperature -30.0 °C
90.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-2
Melting Point 166 °C
331 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
Cavity temperature
<= 205 °C
<= 401 °F
to avoid burning and discoloring product
Zone 1 170 - 180 °C
338 - 356 °F
Zone 2 180 - 190 °C
356 - 374 °F
Zone 3 180 - 190 °C
356 - 374 °F
Zone 4 180 - 200 °C
356 - 392 °F
Die Temperature 180 - 200 °C
356 - 392 °F
Melt Temperature 180 - 200 °C
356 - 392 °F
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Dry Time 3.00 hour
3.00 hour
Injection Pressure 60.0 - 120 MPa
8700 - 17400 psi
Hold Pressure 60.0 - 120 MPa
8700 - 17400 psi
Back Pressure 0.500 MPa
72.5 psi
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed slow
Pre-drying Drying is not normally required with proper storage
Processing conditions ISO 9988-2
Profile extrusion Yes