Celanese Hostaform® MR130HPB POM, Specialty  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name Hostaform®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Hostaform® MR130HPB POM, Specialty  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary Data SheetMedia resistant - bleach, high modulus gradeInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 190 °C
13 g/10 min

@Load 4.76 lb,
Temperature 374 °F
(MVR) cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 69.0 MPa
10000 psi
50mm/min; ISO 527-2/1A
Elongation at Yield 9.0 %
9.0 %
50mm/min; ISO 527-2/1A
Tensile Modulus 3.10 GPa
450 ksi
1mm/min; ISO 527-2/1A
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Charpy Impact, Notched 0.650 J/cm²
3.09 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-2
Melting Point 170 °C
338 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
80.0 - 120 °C
176 - 248 °F
Cavity temperature
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Zone 1 170 - 180 °C
338 - 356 °F
Zone 2 180 - 190 °C
356 - 374 °F
Zone 3 180 - 200 °C
356 - 392 °F
Zone 4 180 - 210 °C
356 - 410 °F
Die Temperature 180 - 210 °C
356 - 410 °F
Melt Temperature 190 - 230 °C
374 - 446 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Drying Temperature 100 °C
212 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Pressure 60.0 - 120 MPa
8700 - 17400 psi
Hold Pressure 60.0 - 120 MPa
8700 - 17400 psi
Back Pressure 0.500 MPa
72.5 psi
Hot-Working Temperature 190 - 210 °C
374 - 410 °F
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed slow
Longer pre-drying times/storage The product can then be stored in standard conditions until processed.
Pre-drying Drying is suggested, depending on handling