Celanese Hostaform® C 2521 XAP2 ® POM

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer Celanese Corporation
Trade Name Hostaform®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Hostaform® C 2521 XAP2 ® POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Stiff-flowing type for injection molding and extrusion with high impact toughness and good tracking resistance over a high range of temperature; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. With reduced emissions especially for automotive interior application. Burning rate according to FMVSS 302
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Melt Density 1.20 g/cc
0.0434 lb/in³
Water Absorption 0.65 %
0.65 %
ISO 62
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 18.0 MPa

@Strain 2.00 %,
Temperature 80.0 °C
2610 psi

@Strain 2.00 %,
Temperature 176 °F
21.0 MPa

@Strain 2.00 %,
Temperature 60.0 °C
3050 psi

@Strain 2.00 %,
Temperature 140 °F
23.0 MPa

@Strain 4.00 %,
Temperature 80.0 °C
3340 psi

@Strain 4.00 %,
Temperature 176 °F
25.0 MPa

@Strain 6.00 %,
Temperature 80.0 °C
3630 psi

@Strain 6.00 %,
Temperature 176 °F
26.0 MPa

@Strain 8.00 %,
Temperature 80.0 °C
3770 psi

@Strain 8.00 %,
Temperature 176 °F
29.0 MPa

@Strain 2.00 %,
Temperature 40.0 °C
4210 psi

@Strain 2.00 %,
Temperature 104 °F
32.0 MPa

@Strain 4.00 %,
Temperature 60.0 °C
4640 psi

@Strain 4.00 %,
Temperature 140 °F
35.0 MPa

@Strain 2.00 %,
Temperature 23.0 °C
5080 psi

@Strain 2.00 %,
Temperature 73.4 °F
38.0 MPa

@Strain 6.00 %,
Temperature 60.0 °C
5510 psi

@Strain 6.00 %,
Temperature 140 °F
39.0 MPa

@Strain 8.00 %,
Temperature 60.0 °C
5660 psi

@Strain 8.00 %,
Temperature 140 °F
40.0 MPa

@Strain 4.00 %,
Temperature 40.0 °C
5800 psi

@Strain 4.00 %,
Temperature 104 °F
45.0 MPa

@Strain 6.00 %,
Temperature 40.0 °C
6530 psi

@Strain 6.00 %,
Temperature 104 °F
46.0 MPa

@Strain 8.00 %,
Temperature 40.0 °C
6670 psi

@Strain 8.00 %,
Temperature 104 °F
50.0 MPa

@Strain 4.00 %,
Temperature 23.0 °C
7250 psi

@Strain 4.00 %,
Temperature 73.4 °F
55.0 MPa

@Strain 6.00 %,
Temperature 23.0 °C
7980 psi

@Strain 6.00 %,
Temperature 73.4 °F
56.0 MPa

@Strain 8.00 %,
Temperature 23.0 °C
8120 psi

@Strain 8.00 %,
Temperature 73.4 °F
60.0 MPa

@Strain 2.00 %,
Temperature -40.0 °C
8700 psi

@Strain 2.00 %,
Temperature -40.0 °F
81.0 MPa

@Strain 4.00 %,
Temperature -40.0 °C
11700 psi

@Strain 4.00 %,
Temperature -40.0 °F
94.0 MPa

@Strain 6.00 %,
Temperature -40.0 °C
13600 psi

@Strain 6.00 %,
Temperature -40.0 °F
10.0 MPa

@Strain 1.00 %,
Time 3.60e+7 sec
1450 psi

@Strain 1.00 %,
Time 10000 hour
11.0 MPa

@Strain 1.00 %,
Time 3.60e+6 sec
1600 psi

@Strain 1.00 %,
Time 1000 hour
14.0 MPa

@Strain 1.00 %,
Time 360000 sec
2030 psi

@Strain 1.00 %,
Time 100 hour
16.0 MPa

@Strain 1.00 %,
Time 36000 sec
2320 psi

@Strain 1.00 %,
Time 10.0 hour
17.0 MPa

@Strain 2.00 %,
Time 3.60e+7 sec
2470 psi

@Strain 2.00 %,
Time 10000 hour
19.0 MPa

@Time 3600 sec,
Strain 1.00 %
2760 psi

@Time 1.00 hour,
Strain 1.00 %
20.0 MPa

@Strain 2.00 %,
Time 3.60e+6 sec
2900 psi

@Strain 2.00 %,
Time 1000 hour
23.0 MPa

@Strain 3.00 %,
Time 3.60e+7 sec
3340 psi

@Strain 3.00 %,
Time 10000 hour
23.0 MPa

@Strain 2.00 %,
Time 360000 sec
3340 psi

@Strain 2.00 %,
Time 100 hour
25.0 MPa

@Strain 3.00 %,
Time 3.60e+6 sec
3630 psi

@Strain 3.00 %,
Time 1000 hour
26.0 MPa

@Strain 2.00 %,
Time 36000 sec
3770 psi

@Strain 2.00 %,
Time 10.0 hour
26.0 MPa

@Strain 4.00 %,
Time 3.60e+7 sec
3770 psi

@Strain 4.00 %,
Time 10000 hour
28.0 MPa

@Strain 5.00 %,
Time 3.60e+7 sec
4060 psi

@Strain 5.00 %,
Time 10000 hour
28.0 MPa

@Strain 3.00 %,
Time 360000 sec
4060 psi

@Strain 3.00 %,
Time 100 hour
29.0 MPa

@Time 3600 sec,
Strain 2.00 %
4210 psi

@Time 1.00 hour,
Strain 2.00 %
29.0 MPa

@Strain 4.00 %,
Time 3.60e+6 sec
4210 psi

@Strain 4.00 %,
Time 1000 hour
Tensile Strength, Yield 62.0 MPa
8990 psi
50 mm/min; ISO 527-2/1A
Elongation at Break 35 %
35 %
50 mm/min; ISO 527-2/1A
Elongation at Yield 9.0 %
9.0 %
50 mm/min; ISO 527-2/1A
Tensile Modulus 2.45 GPa
355 ksi
1 mm/min; ISO 527-2/1A
Shear Modulus 80.0 GPa

@Temperature 150 °C
11600 ksi

@Temperature 302 °F
180 GPa

@Temperature 100 °C
26100 ksi

@Temperature 212 °F
300 GPa

@Temperature 50.0 °C
43500 ksi

@Temperature 122 °F
990 GPa

@Temperature 0.000 °C
144000 ksi

@Temperature 32.0 °F
1200 GPa

@Temperature -50.0 °C
174000 ksi

@Temperature -58.0 °F
Secant Modulus 0.400 GPa

@Strain 8.00 %,
Temperature 80.0 °C
58.0 ksi

@Strain 8.00 %,
Temperature 176 °F
0.500 GPa

@Strain 8.00 %,
Temperature 60.0 °C
72.5 ksi

@Strain 8.00 %,
Temperature 140 °F
0.500 GPa

@Strain 6.00 %,
Temperature 80.0 °C
72.5 ksi

@Strain 6.00 %,
Temperature 176 °F
0.600 GPa

@Strain 4.00 %,
Temperature 80.0 °C
87.0 ksi

@Strain 4.00 %,
Temperature 176 °F
0.600 GPa

@Strain 8.00 %,
Temperature 40.0 °C
87.0 ksi

@Strain 8.00 %,
Temperature 104 °F
0.650 GPa

@Strain 6.00 %,
Temperature 60.0 °C
94.3 ksi

@Strain 6.00 %,
Temperature 140 °F
0.700 GPa

@Strain 4.00 %,
Temperature 60.0 °C
102 ksi

@Strain 4.00 %,
Temperature 140 °F
0.750 GPa

@Strain 8.00 %,
Temperature 23.0 °C
109 ksi

@Strain 8.00 %,
Temperature 73.4 °F
0.750 GPa

@Strain 6.00 %,
Temperature 40.0 °C
109 ksi

@Strain 6.00 %,
Temperature 104 °F
0.800 GPa

@Strain 2.00 %,
Temperature 80.0 °C
116 ksi

@Strain 2.00 %,
Temperature 176 °F
1.00 GPa

@Strain 4.00 %,
Temperature 40.0 °C
145 ksi

@Strain 4.00 %,
Temperature 104 °F
1.20 GPa

@Strain 2.00 %,
Temperature 60.0 °C
174 ksi

@Strain 2.00 %,
Temperature 140 °F
1.25 GPa

@Strain 4.00 %,
Temperature 23.0 °C
181 ksi

@Strain 4.00 %,
Temperature 73.4 °F
1.40 GPa

@Strain 2.00 %,
Temperature 40.0 °C
203 ksi

@Strain 2.00 %,
Temperature 104 °F
1.50 GPa

@Strain 6.00 %,
Temperature -40.0 °C
218 ksi

@Strain 6.00 %,
Temperature -40.0 °F
1.80 GPa

@Strain 2.00 %,
Temperature 23.0 °C
261 ksi

@Strain 2.00 %,
Temperature 73.4 °F
1.85 GPa

@Strain 6.00 %,
Temperature 23.0 °C
268 ksi

@Strain 6.00 %,
Temperature 73.4 °F
2.00 GPa

@Strain 4.00 %,
Temperature -40.0 °C
290 ksi

@Strain 4.00 %,
Temperature -40.0 °F