Celanese FORTRON MT9140L4 PPS, 40% Medical Technology

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer Celanese Corporation
Trade Name FORTRON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON MT9140L4 PPS, 40% Medical Technology.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fortron MT 9140L4 is a 40% glass fiber reinforced injection molding grade that exhibits excellent heat and chemical resistance, inherent flame retardancy, and high hardness and rigidity at elevated temperatures.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
ISO 1183
Water Absorption at Saturation 0.0200 %
0.0200 %
ISO 62
Linear Mold Shrinkage, Flow 0.00200 - 0.00600 cm/cm
0.00200 - 0.00600 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00400 - 0.00600 cm/cm
0.00400 - 0.00600 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
ISO 2039-2
Tensile Strength at Break 190 MPa
27600 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.80 %
1.80 %
5mm/min; ISO 527-2/1A
Flexural Strength 280 MPa
40600 psi
ISO 178
Flexural Modulus 14.0 GPa
2030 ksi
ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180/1A
32.0 kJ/m²

@Temperature 23.0 °C
15.2 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 4.80 J/cm²
22.8 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 280 °C
536 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 200 °C
392 °F
ISO 75-1, -2
Glass Transition Temp, Tg 90.0 °C
194 °F
ISO 11357-1,-2,-3
Processing Properties Metric English Comments
Processing Temperature 140 - 160 °C
284 - 320 °F
cavity
330 - 340 °C
626 - 644 °F
hot runner
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 290 - 300 °C
554 - 572 °F
Zone 2 310 - 320 °C
590 - 608 °F
Zone 3 330 - 340 °C
626 - 644 °F
Zone 4 330 - 340 °C
626 - 644 °F
Die Temperature 310 - 330 °C
590 - 626 °F
Melt Temperature 310 - 340 °C
590 - 644 °F
ISO 294
330 - 340 °C
626 - 644 °F
Mold Temperature 135 - 160 °C
275 - 320 °F
ISO 294
Drying Temperature 130 - 140 °C
266 - 284 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Injection Pressure 50.0 - 100 MPa
7250 - 14500 psi
Hold Pressure 30.0 - 70.0 MPa
4350 - 10200 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 50.0 rpm

@Diameter 55.0 mm
50.0 rpm

@Diameter 2.17 in
75.0 rpm

@Diameter 40.0 mm
75.0 rpm

@Diameter 1.57 in
120 rpm

@Diameter 25.0 mm
120 rpm

@Diameter 0.984 in
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed fast
Sheet extrusion No