Celanese FORTRON ICE 717F PPS, 65% Mineral / Glass Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
Manufacturer Celanese Corporation
Trade Name FORTRON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON ICE 717F PPS, 65% Mineral / Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fortron ICE 717F is a glass/mineral reinforced material with superior fuel resistance. It is specially designed to work in the environment of high temperature and high ethanol content. It offiers excellent physical properites similar to those of the Fortron standard glass/mineral reinforced products.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.981 g/cc
0.07157 lb/in³
ISO 1183
Water Absorption at Saturation 0.190 %
0.190 %
ISO 62
Linear Mold Shrinkage, Flow 0.00110 - 0.00160 cm/cm
0.00110 - 0.00160 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00180 - 0.00230 cm/cm
0.00180 - 0.00230 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 102
102
ISO 2039-2
Tensile Strength at Break 135 MPa
19600 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.10 %
1.10 %
5mm/min; ISO 527-2/1A
Flexural Strength 210 MPa
30500 psi
ISO 178
Flexural Modulus 18.5 GPa
2680 ksi
ISO 178
Izod Impact, Notched (ISO) 5.60 kJ/m²

@Temperature -30.0 °C
2.66 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
22.0 kJ/m²

@Temperature 23.0 °C
10.5 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 2.20 J/cm²
10.5 ft-lb/in²
ISO 179/1eU
2.40 J/cm²

@Temperature -30.0 °C
11.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179/1eA
0.490 J/cm²

@Temperature -30.0 °C
2.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 16.0 µm/m-°C
8.89 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ISO 11359-2
Melting Point 280 °C
536 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 277 °C
531 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 235 °C
455 °F
ISO 75-1, -2
Glass Transition Temp, Tg 90.0 °C
194 °F
ISO 11357-1,-2,-3
Processing Properties Metric English Comments
Processing Temperature 90.0 - 160 °C
194 - 320 °F
cavity
330 - 340 °C
626 - 644 °F
hot runner
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 290 - 300 °C
554 - 572 °F
Zone 2 310 - 320 °C
590 - 608 °F
Zone 3 330 - 340 °C
626 - 644 °F
Zone 4 330 - 340 °C
626 - 644 °F
Die Temperature 310 - 330 °C
590 - 626 °F
Melt Temperature 330 - 340 °C
626 - 644 °F
Drying Temperature 130 - 140 °C
266 - 284 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Injection Pressure 50.0 - 100 MPa
7250 - 14500 psi
Hold Pressure 30.0 - 70.0 MPa
4350 - 10200 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 50.0 rpm

@Diameter 55.0 mm
50.0 rpm

@Diameter 2.17 in
75.0 rpm

@Diameter 40.0 mm
75.0 rpm

@Diameter 1.57 in
120 rpm

@Diameter 25.0 mm
120 rpm

@Diameter 0.984 in
Descriptive Properties Value Comments
Injection Speed fast