Celanese FORTRON FX4382T1 PPS, Impact Modified  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name FORTRON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON FX4382T1 PPS, Impact Modified  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fortron FX4382T1 is an impact-modified, unreinforced, extrusion grade offering high tensile elongation. Recommended processing conditions are identical to our standard unfilled grades.Unreinforced, impact-modified extrusion grade.Information provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.264 g/cc
1.264 g/cc
ASTM D792
Density 1.275 g/cc
0.04606 lb/in³
ISO 1183
Water Absorption 0.035 %
0.035 %
ISO 62
0.030 %

@Temperature -17.8 °C
0.030 %

@Temperature 0.000 °F
24hr immersion; ASTM D570
Linear Mold Shrinkage, Flow 0.0090 - 0.014 cm/cm
0.0090 - 0.014 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 - 0.014 cm/cm
0.0070 - 0.014 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 41
41
ASTM D785
Tensile Strength at Break 50.0 MPa
7250 psi
5mm/min; ISO 527-2/1A
Tensile Strength, Yield 53.9 MPa
7820 psi
ASTM D638
12.6 MPa

@Temperature 121 °C
1830 psi

@Temperature 250 °F
ASTM D638
87.01 MPa

@Temperature -40.0 °C
12620 psi

@Temperature -40.0 °F
ASTM D638
Elongation at Break 25 %
25 %
5mm/min; ISO 527-2/1A
10 %

@Temperature -40.0 °C
10 %

@Temperature -40.0 °F
ASTM D638
25 %

@Temperature 22.8 °C
25 %

@Temperature 73.0 °F
ASTM D638
95 %

@Temperature 121 °C
95 %

@Temperature 250 °F
ASTM D638
96 %

@Temperature 204 °C
96 %

@Temperature 400 °F
ASTM D638
Elongation at Yield 6.0 %

@Temperature -40.0 °C
6.0 %

@Temperature -40.0 °F
ASTM D638
6.0 %

@Temperature 22.8 °C
6.0 %

@Temperature 73.0 °F
ASTM D638
30 %

@Temperature 121 °C
30 %

@Temperature 250 °F
ASTM D638
Tensile Modulus 2.80 GPa
406 ksi
1mm/min; ISO 527-2/1A
0.138 GPa

@Temperature 200 °C
20.0 ksi

@Temperature 392 °F
ASTM D638
0.345 GPa

@Temperature 121 °C
50.0 ksi

@Temperature 250 °F
ASTM D638
2.41 GPa

@Temperature 22.8 °C
350 ksi

@Temperature 73.0 °F
ASTM D638
3.41 GPa

@Temperature -40.0 °C
495 ksi

@Temperature -40.0 °F
ASTM D638
Flexural Strength 79.3 MPa
11500 psi
ASTM D790
Flexural Modulus 0.283 GPa

@Temperature 121 °C
41.0 ksi

@Temperature 250 °F
ASTM D790
2.14 GPa

@Temperature 22.8 °C
310 ksi

@Temperature 73.0 °F
ASTM D790
Izod Impact, Notched 5.07 J/cm
9.50 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Charpy Impact, Notched 3.00 J/cm²
14.3 ft-lb/in²
ISO 179/1eA
Impact Test 61.0 J

@Temperature 22.8 °C
45.0 ft-lb

@Temperature 73.0 °F
Multiaxial impact str (Dynatup) tot energy ft-lbs; ASTM D3763
Coefficient of Friction, Dynamic 0.20
0.20
steel; Internal
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C
33.3 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 77.0 µm/m-°C
42.8 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 81.7 °C
179 °F
ASTM D648
100 °C
212 °F
ISO 75-1, -2
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+16 ohm-cm
5.00e+16 ohm-cm
IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+9 Hz
3.3

@Frequency 1.00e+9 Hz
ASTM D150
Comparative Tracking Index 150 V
150 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
140 - 160 °C
284 - 320 °F
Cavity temperature
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Zone 1 290 - 300 °C
554 - 572 °F
Zone 2 300 - 310 °C
572 - 590 °F
Zone 3 310 - 320 °C
590 - 608 °F
Zone 4 310 - 320 °C
590 - 608 °F
Die Temperature 300 - 310 °C
572 - 590 °F
Melt Temperature 310 - 320 °C
590 - 608 °F
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Pressure 40.0 - 80.0 MPa
5800 - 11600 psi
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Back Pressure 3.00 MPa
435 psi
Screw Speed 50 rpm

@Diameter 55.0 mm
50 rpm

@Diameter 2.17 in
75 rpm

@Diameter 40.0 mm
75 rpm

@Diameter 1.57 in
120 rpm

@Diameter 25.0 mm
120 rpm

@Diameter 0.984 in
Hot-Working Temperature 310 - 320 °C
590 - 608 °F