Celanese FORTRON 6341L4 PPS, 40% Specialty

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer Celanese Corporation
Trade Name FORTRON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON 6341L4 PPS, 40% Specialty.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fortron 6341L4 is a tribological-modified Fortron«-PPS containing 40% glass fibre. Fortron 6341L4 comprises the same mechanical properties like Fortron 1342L4, but with a different tribological adjustment.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.70 g/cc
0.0614 lb/in³
ISO 1183
Water Absorption at Saturation 0.0200 %
0.0200 %
ISO 62
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa
23900 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.60 %
1.60 %
5mm/min; ISO 527-2/1A
Tensile Modulus 14.4 GPa
2090 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 245 MPa
35500 psi
ISO 178
Flexural Modulus 13.7 GPa
1990 ksi
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359-2
Melting Point 280 °C
536 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 215 °C
419 °F
ISO 75-1, -2
Glass Transition Temp, Tg 90.0 °C
194 °F
ISO 11357-1,-2,-3
Processing Properties Metric English Comments
Processing Temperature 140 - 160 °C
284 - 320 °F
cavity
330 - 340 °C
626 - 644 °F
hot runner
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 290 - 300 °C
554 - 572 °F
Zone 2 310 - 320 °C
590 - 608 °F
Zone 3 330 - 340 °C
626 - 644 °F
Zone 4 330 - 340 °C
626 - 644 °F
Die Temperature 310 - 330 °C
590 - 626 °F
Melt Temperature 330 - 340 °C
626 - 644 °F
Drying Temperature 130 - 140 °C
266 - 284 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Pressure 50.0 - 100 MPa
7250 - 14500 psi
Hold Pressure 30.0 - 70.0 MPa
4350 - 10200 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 50.0 rpm

@Diameter 55.0 mm
50.0 rpm

@Diameter 2.17 in
75.0 rpm

@Diameter 40.0 mm
75.0 rpm

@Diameter 1.57 in
120 rpm

@Diameter 25.0 mm
120 rpm

@Diameter 0.984 in