Celanese FORTRON 6160B4 PPS, 60% Mineral / Glass Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
Manufacturer Celanese Corporation
Trade Name FORTRON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON 6160B4 PPS, 60% Mineral / Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fortron 6160B4 has excellent heat and chemical resistance as well as good electrical properties. This product is inherently flame-retardant and offers high hardness and rigidity. 6160B4 has demonstrated excellent performance in hot runner systems and superior contact corrosion resistance. Applications include electronic components (i.e. molded in lead frames, contacts or pins).Information provided by Celanese
Physical Properties Metric English Comments
Density 1.90 g/cc
0.0686 lb/in³
ISO 1183
Water Absorption at Saturation 0.0200 %
0.0200 %
ISO 62
Linear Mold Shrinkage, Flow 0.00200 - 0.00600 cm/cm
0.00200 - 0.00600 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00300 - 0.00700 cm/cm
0.00300 - 0.00700 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
ISO 2039-2
Tensile Strength at Break 145 MPa
21000 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.00 %
1.00 %
5mm/min; ISO 527-2/1A
Tensile Modulus 17.3 GPa
2510 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 220 MPa
31900 psi
ISO 178
Flexural Modulus 16.7 GPa
2420 ksi
ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
Charpy Impact Unnotched 2.70 J/cm²
12.8 ft-lb/in²
ISO 179/1eU
2.70 J/cm²

@Temperature -30.0 °C
12.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 280 °C
536 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 220 °C
428 °F
ISO 75-1, -2
Glass Transition Temp, Tg 90.0 °C
194 °F
ISO 11357-1,-2,-3
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 0.810 mm
V-0

@Thickness 0.0319 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 4.90

@Frequency 1.00e+6 Hz
4.90

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 26.0 kV/mm
660 kV/in
IEC 60243-1
Dissipation Factor 0.00100

@Frequency 1.00e+6 Hz
0.00100

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 175 V
175 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 140 - 160 °C
284 - 320 °F
cavity
330 - 340 °C
626 - 644 °F
hot runner
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 290 - 300 °C
554 - 572 °F
Zone 2 310 - 320 °C
590 - 608 °F
Zone 3 330 - 340 °C
626 - 644 °F
Zone 4 330 - 340 °C
626 - 644 °F
Die Temperature 310 - 330 °C
590 - 626 °F
Melt Temperature 310 - 340 °C
590 - 644 °F
ISO 294
330 - 340 °C
626 - 644 °F
Mold Temperature 135 - 160 °C
275 - 320 °F
ISO 294
Drying Temperature 130 - 140 °C
266 - 284 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Injection Pressure 50.0 - 100 MPa
7250 - 14500 psi
Hold Pressure 30.0 - 70.0 MPa
4350 - 10200 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 50.0 rpm

@Diameter 55.0 mm
50.0 rpm

@Diameter 2.17 in
75.0 rpm

@Diameter 40.0 mm
75.0 rpm

@Diameter 1.57 in
120 rpm

@Diameter 25.0 mm
120 rpm

@Diameter 0.984 in
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed fast
Sheet extrusion No