Celanese FORTRON 205 PPS  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name FORTRON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON 205 PPS  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
0205 is an easy flowing unfilled grade. It demonstrates excellent chemical resistance and thermal stability. Intended for compounding with various fillers. Available standard in pellet (0205P4) and powder (0205B4) form.Medium-range viscosity, for compoundingOn injection molding machines with 15-25 D long three-section screws, are usual in the trade, the unreinforced FORTRON is processable. A shut-off nozzle is recommended.Information provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D792
1.41 g/cc
1.41 g/cc
ASTM D792
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
1.40 g/cc
0.0505 lb/in³
ASTM D792
Water Absorption 0.020 %
0.020 %
ISO 62
0.030 %
0.030 %
24hr immersion; ASTM D570
Linear Mold Shrinkage, Flow 0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
ASTM D955
0.012 - 0.015 cm/cm
0.012 - 0.015 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
ASTM D955
0.015 - 0.018 cm/cm
0.015 - 0.018 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 93
93
ASTM D785
95
95
ISO 2039-2
Tensile Strength at Break 66.0 MPa
9570 psi
5mm/min; ISO 527-2/1A
86.2 MPa
12500 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
5mm/min; ISO 527-2/1A
Tensile Modulus 4.00 GPa
580 ksi
1mm/min; ISO 527-2/1A
Flexural Strength 0.896 MPa
130 psi
ISO 178
145 MPa
21000 psi
ASTM D790
Flexural Modulus 3.90 GPa
566 ksi
ISO 178
4.14 GPa

@Temperature 22.8 °C
600 ksi

@Temperature 73.0 °F
ASTM D790
Izod Impact, Notched 0.267 J/cm
0.500 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.87 J/cm
11.0 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 2.00 kJ/m²
0.952 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear 53.0 µm/m-°C
29.4 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 52.0 µm/m-°C
28.9 µin/in-°F
ISO 11359-2
Specific Heat Capacity 1.83 J/g-°C
0.437 BTU/lb-°F
Internal
Melting Point 280 °C
536 °F
10°C/min; ISO 11357-1,-2,-3
Transformation Temperature, Tg 90.0 °C
194 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 204 °C
400 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
220 °F
ASTM D648
115 °C
239 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 95.0 °C
203 °F
ISO 75-1, -2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm
1.00e+11 ohm-cm
IEC 60093
1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
ASTM D150
3.0

@Frequency 1000 Hz
3.0

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 17.0 kV/mm
432 kV/in
IEC 60243-1
Dissipation Factor 0.00090

@Frequency 1.00e+6 Hz
0.00090

@Frequency 1.00e+6 Hz
ASTM D150
0.0010

@Frequency 1000 Hz
0.0010

@Frequency 1000 Hz
ASTM D150
Arc Resistance 124 sec
124 sec
ASTM D495
Comparative Tracking Index 100 V
100 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
140 - 160 °C
284 - 320 °F
Cavity temperature
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Zone 1 290 - 300 °C
554 - 572 °F
Zone 2 300 - 310 °C
572 - 590 °F
Zone 3 310 - 320 °C
590 - 608 °F
Zone 4 310 - 320 °C
590 - 608 °F
Die Temperature 300 - 310 °C
572 - 590 °F
Melt Temperature 295 - 330 °C
563 - 626 °F
Injection molding; ISO 294
310 - 320 °C
590 - 608 °F
Mold Temperature >= 140 °C
>= 284 °F
135 - 160 °C
275 - 320 °F
Injection molding; ISO 294
Drying Temperature 110 - 120 °C
230 - 248 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Moisture Content 0.020 %
0.020 %
Necessary low maximum residual
Dew Point <= -30.0 °C
<= -22.0 °F
Pre-drying
Injection Pressure 40.0 - 80.0 MPa
5800 - 11600 psi
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Back Pressure 3.00 MPa
435 psi
Screw Speed 50 rpm

@Diameter 55.0 mm
50 rpm

@Diameter 2.17 in
75 rpm

@Diameter 40.0 mm
75 rpm

@Diameter 1.57 in
120 rpm

@Diameter 25.0 mm
120 rpm

@Diameter 0.984 in
Hot-Working Temperature 310 - 320 °C
590 - 608 °F