Celanese FORTRON 1200L1 PPS, Specialty  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name FORTRON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON 1200L1 PPS, Specialty  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fortron 1200L1 is an unfilled grade for extrusion applications, which has a high melt viscosity and tensile elongation. The recommended processing conditions are identical to those of our standard unfilled grades.Unfilled extrusion grade that has a high melt viscosity and tensile elongation.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Water Absorption 0.020 %
0.020 %
ISO 62
Viscosity 430000 cP
430000 cP
Internal
Mechanical Properties Metric English Comments
Hardness, Rockwell M 93
93
ISO 2039-2
Tensile Strength at Break 88.0 MPa
12800 psi
50mm/min; ISO 527-2/1A
Elongation at Break 15 %
15 %
50mm/min; ISO 527-2/1A
Elongation at Yield 3.0 %
3.0 %
50mm/min; ISO 527-2/1A
Tensile Modulus 4.00 GPa
580 ksi
1mm/min; ISO 527-2/1A
Flexural Strength 141 MPa
20500 psi
ISO 178
Flexural Modulus 4.10 GPa
595 ksi
ISO 178
Charpy Impact Unnotched 20.0 J/cm²
95.2 ft-lb/in²
ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 42.0 µm/m-°C
23.3 µin/in-°F
ISO 11359-2
Melting Point 275 °C
527 °F
10°C/min; ISO 11357-1,-2,-3
Transformation Temperature, Tg 90.0 °C
194 °F
10°C/min; ISO 11357-1,-2,-3
Electrical Properties Metric English Comments
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
ASTM D150
3.0

@Frequency 10000 Hz
3.0

@Frequency 10000 Hz
ASTM D150
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243-1
Processing Properties Metric English Comments
Drying Temperature 110 - 120 °C
230 - 248 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Moisture Content 0.020 %
0.020 %
Necessary low maximum residual
Descriptive Properties Value Comments
Injection molding Yes
Sheet extrusion Yes