Celanese FORTRON 1140L7 PPS, 40% Glass Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer Celanese Corporation
Trade Name FORTRON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON 1140L7 PPS, 40% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
One of the easiest flowing 40% glass reinforced grade in the Fortron product line. This material can be processed at fast cycle times due to the unique crystallization characteristics. This product offers good heat and chemical resistance, as well as, good electrical properties. The product is inherently flame-retardant and exhibits high hardness and rigidity.Information provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.64 g/cc
1.64 g/cc
ASTM D792
Density 0.000948 g/cc
0.0000343 lb/in³
ASTM D792
1.65 g/cc
0.0596 lb/in³
ISO 1183
Water Absorption 0.0300 %

@Temperature 22.8 °C
0.0300 %

@Temperature 73.0 °F
24hr immersion; ASTM D570
Water Absorption at Saturation 0.0200 %
0.0200 %
ISO 62
Linear Mold Shrinkage, Flow 0.00200 cm/cm
0.00200 in/in
ASTM D955
0.00100 - 0.00300 cm/cm
0.00100 - 0.00300 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00500 cm/cm
0.00500 in/in
ASTM D955
0.00500 - 0.00700 cm/cm
0.00500 - 0.00700 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
ISO 2039-2
103
103
ASTM D785
Tensile Strength at Break 145 MPa
21000 psi
ASTM D638
170 MPa
24700 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.20 %
1.20 %
ASTM D638
1.60 %
1.60 %
5mm/min; ISO 527-2/1A
Tensile Modulus 14.5 GPa
2100 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 207 MPa
30000 psi
ASTM D790
260 MPa
37700 psi
ISO 178
Flexural Modulus 14.5 GPa
2100 ksi
ASTM D790
14.5 GPa
2100 ksi
ISO 178
Izod Impact, Notched 0.747 J/cm
1.40 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.68 J/cm
6.90 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
Thermal Properties Metric English Comments
Melting Point 280 °C
536 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
ASTM D648
270 °C
518 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 200 °C
392 °F
ISO 75-1, -2
Glass Transition Temp, Tg 90.0 °C
194 °F
ISO 11357-1,-2,-3
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 0.380 mm
V-0

@Thickness 0.0150 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.70

@Frequency 1000 Hz
3.70

@Frequency 1000 Hz
ASTM D150
3.70

@Frequency 1.00e+6 Hz
3.70

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 26.0 kV/mm
660 kV/in
IEC 60243-1
Dissipation Factor 0.00100

@Frequency 1000 Hz
0.00100

@Frequency 1000 Hz
ASTM D150
0.00100

@Frequency 1.00e+6 Hz
0.00100

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 134 sec
134 sec
ASTM D495
Comparative Tracking Index 125 V
125 V
IEC 60112
150 V
150 V
ASTM D3638
Processing Properties Metric English Comments
Processing Temperature 140 - 160 °C
284 - 320 °F
cavity
330 - 340 °C
626 - 644 °F
hot runner
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 290 - 300 °C
554 - 572 °F
Zone 2 310 - 320 °C
590 - 608 °F
Zone 3 330 - 340 °C
626 - 644 °F
Zone 4 330 - 340 °C
626 - 644 °F
Die Temperature 310 - 330 °C
590 - 626 °F
Melt Temperature 310 - 340 °C
590 - 644 °F
ISO 294
330 - 340 °C
626 - 644 °F
Mold Temperature 135 - 160 °C
275 - 320 °F
ISO 294
Drying Temperature 130 - 140 °C
266 - 284 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Injection Pressure 50.0 - 100 MPa
7250 - 14500 psi
Hold Pressure 30.0 - 70.0 MPa
4350 - 10200 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 50.0 rpm

@Diameter 55.0 mm
50.0 rpm

@Diameter 2.17 in
75.0 rpm

@Diameter 40.0 mm
75.0 rpm

@Diameter 1.57 in
120 rpm

@Diameter 25.0 mm
120 rpm

@Diameter 0.984 in
Descriptive Properties Value Comments