LookPolymers® 1140EC Glass Reinforced Polyphenylene Sulfide (PPS)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer -
Trade Name -
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LookPolymers® 1140EC Glass Reinforced Polyphenylene Sulfide (PPS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Fortron 1140EC offers a unique balance of properties based on a glass reinforced composition, complementing our other fiberglass reinforced product offerings. As with all Fortron grades this product is inherently flame-retardant. Applications include automotive engine cooling components.Information provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 1.67 g/cc
0.0603 lb/in³
ISO 1183
Water Absorption at Saturation 0.020 %
0.020 %
ISO 62
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
ISO 2039-2
Tensile Strength at Break 170 MPa
24700 psi
5 mm/min; ISO 527-2/1A
Elongation at Break 1.35 %
1.35 %
5 mm/min; ISO 527-2/1A
Flexural Strength 255 MPa
37000 psi
ISO 178
Flexural Modulus 16.0 GPa
2320 ksi
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 28.0 kJ/m²
13.3 ft-lb/in²
ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 200 °C
392 °F
ISO 75-1, -2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
IEC 60093
Dielectric Constant 4.0

@Frequency 10000 Hz
4.0

@Frequency 10000 Hz
IEC 60250
Dissipation Factor 0.00020

@Frequency 10000 Hz
0.00020

@Frequency 10000 Hz
IEC 60250
0.0020

@Frequency 1e+6 Hz
0.0020

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 125 V
125 V
IEC 60112