Celanese Coolpoly® D3606 Thermally Conductive Polyamide 4,6  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 46
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Coolpoly® D3606 Thermally Conductive Polyamide 4,6  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CoolPoly D series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The D series is electrically non-conductive and can be used for its dielectric properties.CoolPoly D3606 is a thermally conductive injection molding resin based on a Polyamide 4,6 (PA 4,6) matrix. CoolPoly D3606 is electrically insulative. Thermally conductive polymers like CoolPoly D3606 cool faster than standard injection molding grade resins.Information provided by Cool Polymers, Inc.D3606 has been replaced by D3608
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
ISO 1183
Water Absorption 1.2 %
1.2 %
ISO 62
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D551
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 90.0 MPa
13100 psi
ISO 527-1
Elongation at Break 1.0 %
1.0 %
ISO 527-1
Tensile Modulus 12.0 GPa
1740 ksi
ISO 527-1
Flexural Strength 150 MPa
21800 psi
ISO 178
Flexural Modulus 11.0 GPa
1600 ksi
ISO 178
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179-1
Charpy Impact, Notched 0.450 J/cm²
2.14 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
ASTM E1461
Thermal Conductivity 1.50 W/m-K
10.4 BTU-in/hr-ft²-°F
ASTM E1461
Flammability, UL94 V-0

@Thickness 1.00 mm
V-0

@Thickness 0.0394 in
Processing Properties Metric English Comments
Rear Barrel Temperature 290 - 310 °C
554 - 590 °F
Middle Barrel Temperature 300 - 315 °C
572 - 599 °F
Front Barrel Temperature 305 - 320 °C
581 - 608 °F
Nozzle Temperature 310 - 330 °C
590 - 626 °F
Melt Temperature 310 - 316 °C
590 - 601 °F
Mold Temperature 80.0 - 150 °C
176 - 302 °F
Drying Temperature 104 °C
219 °F
Dry Time 12 hour
12 hour
Moisture Content 0.050 %
0.050 %
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 70.0 - 105 MPa
10200 - 15200 psi
Hold Pressure 35.0 - 70.0 MPa
5080 - 10200 psi
Back Pressure 0.000 - 0.700 MPa
0.000 - 102 psi
Screw Speed 50 - 150 rpm
50 - 150 rpm