Celanese Celstran® TPU-GF30-01-US TPU, 30% Glass Reinforced

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced
Manufacturer Celanese Corporation
Trade Name CELSTRAN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celstran® TPU-GF30-01-US TPU, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% long strand glass fiber reinforced thermoplastic polyurethaneInformation provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.43 g/cc
1.43 g/cc
ASTM D792
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.000500 - 0.00100 cm/cm
0.000500 - 0.00100 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.00150 - 0.00250 cm/cm
0.00150 - 0.00250 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 180 MPa
26100 psi
5mm/min; ISO 527-2/1A
216 MPa
31300 psi
ASTM D638
Elongation at Break 2.75 %
2.75 %
5mm/min; ISO 527-2/1A
2.90 %
2.90 %
ASTM D638
Tensile Modulus 8.50 GPa
1230 ksi
50mm/min; ISO 527-2/1A
9.72 GPa
1410 ksi
ASTM D638
Flexural Strength 270 MPa
39200 psi
ISO 178
272 MPa
39400 psi
ASTM D790
Flexural Modulus 7.70 GPa
1120 ksi
ISO 178
7.79 GPa
1130 ksi
ASTM D790
Izod Impact, Notched 4.38 J/cm
8.20 ft-lb/in
ASTM D256
Charpy Impact, Notched 3.90 J/cm²
18.6 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ISO 75-1, -2
85.0 °C
185 °F
ASTM D648
Processing Properties Metric English Comments
Processing Temperature 70.0 - 90.0 °C
158 - 194 °F
cavity
250 - 260 °C
482 - 500 °F
hot runner
Feed Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Middle Barrel Temperature 70.0 - 80.0 °C
158 - 176 °F
Zone 1 240 - 250 °C
464 - 482 °F
Zone 2 245 - 255 °C
473 - 491 °F
Zone 3 245 - 260 °C
473 - 500 °F
Zone 4 245 - 260 °C
473 - 500 °F
Die Temperature 245 - 260 °C
473 - 500 °F
Melt Temperature 245 - 260 °C
473 - 500 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.0500 %
<= 0.0500 %
Descriptive Properties Value Comments
Injection molding Yes