Celanese Celstran® +PP-GF40-04CN03 PP, 40% Glass Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler
Manufacturer Celanese Corporation
Trade Name CELSTRAN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celstran® +PP-GF40-04CN03 PP, 40% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Material code according to ISO 1043-1: PPInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 135 MPa
19600 psi
5mm/min; ISO 527-2/1A
Tensile Strength 84.0 MPa

@Temperature 80.0 °C
12200 psi

@Temperature 176 °F
ISO 527-1, -2
Elongation at Break 2.00 %
2.00 %
5mm/min; ISO 527-2/1A
2.10 %

@Temperature 80.0 °C
2.10 %

@Temperature 176 °F
ISO 527-1, -2
Tensile Modulus 9.30 GPa
1350 ksi
50mm/min; ISO 527-2/1A
6.60 GPa

@Temperature 80.0 °C
957 ksi

@Temperature 176 °F
ISO 527-1, -2
Flexural Strength 205 MPa
29700 psi
ISO 178
120 MPa

@Temperature 80.0 °C
17400 psi

@Temperature 176 °F
ISO 178
Flexural Modulus 9.20 GPa
1330 ksi
ISO 178
6.70 GPa

@Temperature 80.0 °C
972 ksi

@Temperature 176 °F
ISO 178
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
ISO 179/1eU
5.00 J/cm²

@Temperature -30.0 °C
23.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 3.20 J/cm²
15.2 ft-lb/in²
ISO 179/1eA
3.60 J/cm²

@Temperature -30.0 °C
17.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 158 °C
316 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 138 °C
280 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 30.0 - 70.0 °C
86.0 - 158 °F
cavity
230 - 270 °C
446 - 518 °F
hot runner
Feed Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 220 - 230 °C
428 - 446 °F
Zone 2 230 - 240 °C
446 - 464 °F
Zone 3 240 - 250 °C
464 - 482 °F
Zone 4 >= 250 °C
>= 482 °F
Die Temperature 240 - 250 °C
464 - 482 °F
Melt Temperature 230 - 270 °C
446 - 518 °F
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.200 %
<= 0.200 %
Injection Pressure 60.0 - 120 MPa
8700 - 17400 psi
Hold Pressure 40.0 - 80.0 MPa
5800 - 11600 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 25.0 rpm

@Diameter 75.0 mm
25.0 rpm

@Diameter 2.95 in
35.0 rpm

@Diameter 55.0 mm
35.0 rpm

@Diameter 2.17 in
50.0 rpm

@Diameter 40.0 mm
50.0 rpm

@Diameter 1.57 in
Descriptive Properties Value Comments
Injection Speed slow