Celanese Celstran® PP-GF30-02 PP, 30% Glass Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer Celanese Corporation
Trade Name Celstran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celstran® PP-GF30-02 PP, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% long strand glass fiber reinforced polypropylene30% long strand glass fiber reinforced, chemically coupled polypropyleneInformation provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc
1.12 g/cc
ASTM D792
Density 1.12 g/cc
0.0405 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 92.0 MPa
13300 psi
5mm/min; ISO 527-2/1A
108 MPa
15600 psi
ASTM D638
66.9 MPa

@Temperature 93.3 °C
9700 psi

@Temperature 200 °F
ASTM D638
141 MPa

@Temperature -40.0 °C
20400 psi

@Temperature -40.0 °F
ASTM D638
Elongation at Break 2.53 %
2.53 %
5mm/min; ISO 527-2/1A
2.1 %

@Temperature -40.0 °C
2.1 %

@Temperature -40.0 °F
ASTM D638
2.4 %

@Temperature 22.8 °C
2.4 %

@Temperature 73.0 °F
ASTM D638
2.76 %

@Temperature 93.3 °C
2.76 %

@Temperature 200 °F
ASTM D638
Tensile Modulus 5.80 GPa
841 ksi
1mm/min; ISO 527-2/1A
3.79 GPa

@Temperature 93.3 °C
549 ksi

@Temperature 200 °F
ASTM D638
6.41 GPa

@Temperature 22.8 °C
930 ksi

@Temperature 73.0 °F
ASTM D638
8.69 GPa

@Temperature -40.0 °C
1260 ksi

@Temperature -40.0 °F
ASTM D638
Flexural Strength 155 MPa
22500 psi
ISO 178
157 MPa
22700 psi
ASTM D790
88.9 MPa

@Temperature 121 °C
12900 psi

@Temperature 250 °F
ASTM D790
234 MPa

@Temperature -40.0 °C
34000 psi

@Temperature -40.0 °F
ASTM D790
Flexural Modulus 6.00 GPa
870 ksi
ISO 178
4.25 GPa

@Temperature 121 °C
616 ksi

@Temperature 250 °F
ASTM D790
6.07 GPa

@Temperature 22.8 °C
880 ksi

@Temperature 73.0 °F
ASTM D790
8.34 GPa

@Temperature -40.0 °C
1210 ksi

@Temperature -40.0 °F
ASTM D790
Izod Impact, Notched 2.14 J/cm
4.00 ft-lb/in
ASTM D256
2.72 J/cm

@Temperature -40.0 °C
5.10 ft-lb/in

@Temperature -40.0 °F
ASTM D256
3.58 J/cm

@Temperature 121 °C
6.70 ft-lb/in

@Temperature 250 °F
ASTM D256
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 149 °C
300 °F
ASTM D648
150 °C
302 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 40.0 - 70.0 °C
104 - 158 °F
Cavity temperature
Feed Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 200 - 210 °C
392 - 410 °F
Zone 2 210 - 220 °C
410 - 428 °F
Zone 3 220 - 230 °C
428 - 446 °F
Zone 4 230 - 240 °C
446 - 464 °F
Die Temperature 230 - 240 °C
446 - 464 °F
Melt Temperature 230 - 240 °C
446 - 464 °F
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Dry Time 2.00 hour
2.00 hour
Moisture Content 0.20 %
0.20 %
Necessary low maximum residual
Descriptive Properties Value Comments
Injection molding Yes
Longer pre-drying times/storage Can be stored in standard conditions until processed.
Pre-drying Drying is not normally required with proper storage