Celanese Celstran® PA66-GF50-0112P7,5/10 Nylon 6/66, 50% Glass Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 40% Glass Fiber Reinforced
Manufacturer Celanese Corporation
Trade Name CELSTRAN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celstran® PA66-GF50-0112P7,5/10 Nylon 6/66, 50% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Material code according to ISO 1043-1: PA66Information provided by Celanese
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 220 MPa
31900 psi
5mm/min; ISO 527-2/1A
Tensile Strength 140 MPa

@Temperature 80.0 °C
20300 psi

@Temperature 176 °F
ISO 527-1, -2
Elongation at Break 1.60 %
1.60 %
5mm/min; ISO 527-2/1A
2.40 %

@Temperature 80.0 °C
2.40 %

@Temperature 176 °F
ISO 527-1, -2
Tensile Modulus 16.4 GPa
2380 ksi
50mm/min; ISO 527-2/1A
10.0 GPa

@Temperature 80.0 °C
1450 ksi

@Temperature 176 °F
ISO 527-1, -2
Flexural Strength 300 MPa
43500 psi
ISO 178
250 MPa

@Temperature 80.0 °C
36300 psi

@Temperature 176 °F
ISO 178
Flexural Modulus 14.0 GPa
2030 ksi
ISO 178
Izod Impact, Notched (ISO) 48.0 kJ/m²

@Temperature -30.0 °C
22.8 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1U
57.0 kJ/m²

@Temperature 23.0 °C
27.1 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 6.10 J/cm²
29.0 ft-lb/in²
ISO 179/1eU
5.90 J/cm²

@Temperature -30.0 °C
28.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 3.50 J/cm²
16.7 ft-lb/in²
ISO 179/1eA
3.60 J/cm²

@Temperature -30.0 °C
17.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 240 °C
464 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 220 °C
428 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 90.0 - 120 °C
194 - 248 °F
cavity
300 - 315 °C
572 - 599 °F
hot runner
Feed Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Middle Barrel Temperature 70.0 - 80.0 °C
158 - 176 °F
Zone 1 280 - 285 °C
536 - 545 °F
Zone 2 280 - 290 °C
536 - 554 °F
Zone 3 290 - 300 °C
554 - 572 °F
Zone 4 300 - 310 °C
572 - 590 °F
Die Temperature 310 - 320 °C
590 - 608 °F
Melt Temperature 310 - 320 °C
590 - 608 °F
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Moisture Content <= 0.150 %
<= 0.150 %
Injection Pressure 120 - 150 MPa
17400 - 21800 psi
Hold Pressure 50.0 - 80.0 MPa
7250 - 11600 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 25.0 rpm

@Diameter 75.0 mm
25.0 rpm

@Diameter 2.95 in
35.0 rpm

@Diameter 55.0 mm
35.0 rpm

@Diameter 2.17 in
50.0 rpm

@Diameter 40.0 mm
50.0 rpm

@Diameter 1.57 in
Descriptive Properties Value Comments
Injection Speed medium
UV stabilized/stable to weather Yes