Celanese Celstran® PA66-GF40-07 Nylon 66, 40% Glass Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name CELSTRAN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celstran® PA66-GF40-07 Nylon 66, 40% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40% long fiber glass reinforced, enhanced flow, Nylon 6/6Information provided by Celanese
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 205 MPa
29700 psi
5mm/min; ISO 527-2/1A
Elongation at Break 2.00 %
2.00 %
5mm/min; ISO 527-2/1A
Tensile Modulus 13.0 GPa
1890 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 320 MPa
46400 psi
ISO 178
Flexural Modulus 12.1 GPa
1750 ksi
ISO 178
Charpy Impact, Notched 2.30 J/cm²
10.9 ft-lb/in²
ISO 179/1eA
Processing Properties Metric English Comments
Processing Temperature 80.0 - 100 °C
176 - 212 °F
cavity
Feed Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Middle Barrel Temperature 70.0 - 80.0 °C
158 - 176 °F
Zone 1 285 - 295 °C
545 - 563 °F
Zone 2 290 - 300 °C
554 - 572 °F
Zone 3 300 - 310 °C
572 - 590 °F
Zone 4 300 - 315 °C
572 - 599 °F
Die Temperature 300 - 315 °C
572 - 599 °F
Melt Temperature 300 - 315 °C
572 - 599 °F
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Moisture Content <= 0.180 %