Celanese Celanex® 5214HF PBT, 15% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name Celanex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celanex® 5214HF PBT, 15% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 5214HF is a high flow, 15% glass reinforced, high gloss, flame retardant polyester.Pre-drying: 250F (120C) for 4 HoursInformation provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0060 cm/cm
0.0010 - 0.0060 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039-2
Tensile Strength at Break 77.0 MPa
11200 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.3 %
1.3 %
5mm/min; ISO 527-2/1A
Tensile Modulus 7.20 GPa
1040 ksi
1mm/min; ISO 527-2/1A
Flexural Strength 109 MPa
15800 psi
ISO 178
Flexural Modulus 6.44 GPa
934 ksi
ISO 178
Izod Impact, Notched (ISO) 4.40 kJ/m²
2.09 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 1.70 J/cm²
8.09 ft-lb/in²
ISO 179/1eU
1.50 J/cm²

@Temperature 30.0 °C
7.14 ft-lb/in²

@Temperature 86.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.450 J/cm²
2.14 ft-lb/in²
ISO 179/1eA
0.450 J/cm²

@Temperature 30.0 °C
2.14 ft-lb/in²

@Temperature 86.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 31.0 µm/m-°C
17.2 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 61.0 µm/m-°C
33.9 µin/in-°F
ISO 11359-2
Melting Point 225 °C
437 °F
ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 206 °C
403 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
ISO 75-1, -2
Glass Transition Temp, Tg 55.0 °C
131 °F
ISO 11357-1,-2,-3
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+14 ohm-cm
2.00e+14 ohm-cm
IEC 60093
Surface Resistance 5.00e+15 ohm
5.00e+15 ohm
IEC 60093
Dielectric Constant 3.3

@Frequency 100 Hz
3.3

@Frequency 100 Hz
IEC 60250
3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 15.0 kV/mm
381 kV/in
IEC 60243-1
Dissipation Factor 0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 275 V
275 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 20.0 - 50.0 °C
68.0 - 122 °F
hopper
65.0 - 93.0 °C
149 - 199 °F
cavity
Feed Temperature 230 - 240 °C
446 - 464 °F
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 235 - 250 °C
455 - 482 °F
Zone 3 235 - 250 °C
455 - 482 °F
Zone 4 240 - 255 °C
464 - 491 °F
Die Temperature 250 - 255 °C
482 - 491 °F
Melt Temperature 235 - 255 °C
455 - 491 °F
265 °C
509 °F
ISO 294
Mold Temperature 80.0 °C
176 °F
ISO 294
Moisture Content 0.020 %
0.020 %
Necessary low maximum
Hot-Working Temperature 250 - 260 °C
482 - 500 °F
Descriptive Properties Value Comments
Remarks To avoid discoloration, process temperatures should be kept below 510°F and shear heating should be minimized